Chapter 1.10 - Miscellaneous Etchants

Marvell NanoLab Member login Lab Manual Contents MercuryWeb Berkeley Microlab Chapter Miscellaneous Etchants Table of Contents Aluminum Etchant Type A (Transene Co., Inc.) for VLSI Others Antimony Etchant Aqua Regia Bismuth Etchant Brass Cadmium Sulfide Etchant (CdS) Telluride (CdTe) Chromium Etchant Chromium/Nichrome Etchant Cobalt Columbium Copper Dislocation Etchants Sirtl Secco Wright-Jenkins ASTM Gallium Arsenide Phosphide Germanium Etchant (and Germanium-Silicon) Gold Indium Antimonide Phosphide Tin Oxide (ITO) Iron Etchant Kovar Lead Lucite Magnesium Magnesium Fluoride Mercury Molybdenum (Moly) Monel Nichrome Nichrome Etchant Nickel Nickel Etchant Nickel Oxides Niobium P-Etchant Palladium Miscellaneous Etchants Chapter Picein Wax Piranha Platinum Polish Fairchild s Magic Polish Polysilicon Etchant (see also Silicon Etchant) Preferential Etch (see Dislocation Etchant Wright Jenkins Etchant) Rhodium Ruthenium Silicon Polycrystalline Silicon (Bell Labs) Big Batch Silicon Etch (staff only) Single-Crystal (Sensors) EDP F & K (Finne & Klein) B (Bassous) F (Fast) S (Slow)

Add a small amount of Zn powder (on edge of a spatula). Put the wafer in the solution for about 1 min. Watch for turbidity of the ITO. Transfer the wafer to another beaker containing conc. HCl (no dilution), for about 1 min. Take the wafer out and check if all the film was etched. Return to first solution if needed, at 50 degrees. HCl:HNO

Fullscreen Download
Loading..

Tags:

  Powder

Information

Domain:

Source:

Link to this page:

Please notify us if you found a problem with this document:

Spam in document Broken preview Other abuse

Transcription of Chapter 1.10 - Miscellaneous Etchants

Documents from same domain

Starting material - University of California, Berkeley

nanolab.berkeley.edu

Starting Material Silicon substrate 150 mm, p-type, <100>, 36-63 ohm-cm Attila Horvath 2005. Pad Oxidation and Nitride Deposition Silicon substrate Pad oxide = 250A Silicon nitride = 2200A Attila Horvath 2005. N-Well Photo and Nitride Etch Silicon substrate Pad oxide Silicon nitride

  Material, Starting, Attila, Starting materials

Basic PECVD Plasma Processes (SiH based)

nanolab.berkeley.edu

highly corrosive, please read safety datasheet and safe system of work before use. BHF rate of SiN 0 nm/ min 200 nm/ min 400 nm/ min 600 nm/ min 800 nm/ min 1000 nm/ min 1200 nm/ min 1400 nm/ min 1600 nm/ min 0 °C 200 °C 400 °C 600 °C 800 °C Low rate dep High rate dep Thermal oxide BHF rate of SiO2 0 nm/ min 100 nm/ min 200 nm/ min 300 nm ...

  Safety

Miscellaneous Plating Solutions

nanolab.berkeley.edu

Miscellaneous Plating Solutions . Copper Displacement Plating Solution ... Nickel Plating (Electrodeless) for Ohmic Contacts (W. G. Oldham) JECS 1957, p 226. Nickel Chloride 30 g/L Sodium Hypophosphite 30 g/L . Ammonium Citrate 65 g/L . Ammonium Chloride 50 g/L . …

  Solutions, Nickel, Plating, Plating solution, Nickel plating

Related documents

Acids, Bases and Salts W

www.ncert.nic.in

powder. Add a little water and make a paste. ... which contains zinc carbonate. Soil treatment Excessive use of chemical fertilisers makes the soil acidic. ... the soil is either too acidic or too basic. When the soil is too acidic, it is treated with bases like quick lime (calcium oxide) or slaked lime (calcium hydroxide). If the soil is basic ...

  Powder, Zinc, Oxide

CHAPTER3 Metals and Non-metals - NCERT

ncert.nic.in

oxides, such as aluminium oxide, zinc oxide show both acidic as well as basic behaviour . Such metal oxides which r eact with both acids as well as bases to produce salts and water are known as amphoteric oxides. Aluminium oxide reacts in the following manner with acids and bases – Al 2 O 3 + 6HCl → 2AlCl 3 + 3H 2 O Al 2 O 3 + 2NaOH ...

  Metal, Zinc, Oxide, Zinc oxide

Zinc Coatings - Court Galvanizing, Inc

courtgalvanizinginc.com

remove any oxide that may be on the steel surface. Th e exit end of the furnace is connected with a vacuum chamber, known as a “snout,” to the molten ... the beads to peen the zinc powder onto the part. Th ickness is regulated by the amount of zinc charged to the plating barrel and the duration of tumbling time. After coating, the parts are ...

  Powder, Coating, Zinc, Oxide, Zinc coatings, Zinc powder

SUBJECT GUIDE Heat Treating - ASM International

www.asminternational.org

Oxide Dispersion Strengthening. With this powder metallurgy method, oxides such as yttria or alumina or metals that are strong oxide formers, such as tantalum, are added during the mechani-cal alloying step. They become uniformly distributed through the alloy and impart strength to the component.

  Guide, Subject, Heat, Powder, Oxide, Treating, Subject guide heat treating

Maximum Retail Price List - Berger Paints

www.bergerpaints.com

BP Red Oxide Primer 665 BR ROZC Primer IS2074 435 Berger Red Oxide Primer M62 M92 Zinc Chromate Primer-Yellow BP PRO-Zinc Yellow PRM 3,259 x 707 188 100 2,619 x x x x 2,705 x x x x x x 589 154 83 4,154 x 852 217 121 3,854 x x x x Metal Primers - Solvent Thinnable 077 BP Cement Primer 2,369 1,267 542 148 x

  Lists, Recip, Price list, Zinc, Oxide

Related search queries

Powder, Zinc, Oxide, Metals, Zinc oxide, Zinc Coatings, Zinc powder, SUBJECT GUIDE Heat Treating, Price List