Product Information XAREC EA 522 - Idemitsu Chemicals
Product Information Page 1 of 3 H-470-02-1105-EA522 (Rev 6, May 2011) XAREC EA 522 Crystalline Polymers 22% Glass Filled, Ignition resistant , Impact Modified Polymer for Electronic and Electrical Applications Properties1 Test Method Value Physical Density, g/cm3 ISO 1183 Glass Content, % 22 Water Absorption at 24 hrs. 50% RH, % ISO 62 Mold Shrinkage, flow direction, 2 mm, % IDEMITSU2 Mold Shrinkage, cross flow direction, 2 mm, % IDEMITSU2 Mechanical Tensile Strength at Break, MPa ISO 527 100 Tensile Modulus, MPa ISO 527 8,000 Tensile Elongation at Break, % ISO 527 Flexural Strength, MPa ISO 178 155 Flexural Modulus, MPa ISO 178 7,500 Izod Impact Notched at 23 C, kJ/m2 ISO 180 11 Unnotched at 23 C, kJ/m2 ISO 180 34 Charpy Impact Notched at 23 C, kJ/m2 ISO 179 12 Unnotched at 23 C, kJ/m2 ISO 179 39 Thermal DTUL at MPa, C 80oC tool / 150 oC tool ISO 75 A 225 / 230 DTUL at MPa, C 80oC tool / 150 oC tool ISO 75 B 265 / 265 Coefficient of Linear Thermal Expansion Flow direction, -30 30oC, mm/mm/ C TMA 24 x 10-6 Cross flow direction, -30 - 30oC, mm/mm/oC TMA 53 x 10-6 Electrical Comparative Tracking Index, PLC level IEC 60112, Solution A 1 Dielectric Constant IEC 60250 Volume Resistivity.
Product Information Page 1 of 3 H-470-02-1105-EA522 (Rev 6, May 2011) XAREC® EA 522 Crystalline Polymers – 22% Glass Filled, Ignition Resistant, Impact Modified Polymer for
Tags:
Information
Domain:
Source:
Link to this page:
Please notify us if you found a problem with this document: