Elmax eng 1507/R1601 7 - Uddeholm Global

UDDEHOLM ELMAX SUPERCLEAN 3 Applications New types of engineering plastics, with high filler contents, place greater demands …

  Uddeholm

WELDING OF UDDEHOLM TOOL STEELS

for welding tool steel should be similar in composition to the base material. When welding in the an-nealed condition, e.g. if a mould or die has to be adjusted while in the process of manufacture, it is vital that the filler metal has the same heat treatment characteristics as the base

  Tool, Steel, Welding, Tool steel welding

WELDING OF TOOL STEEL - Uddeholm Global

for welding tool steel should be simi-lar in composition to the base mate-rial. When welding in the annealed condition, e.g. if a mould or die has to be adjusted while in the process of manufacture, it is vital that the filler metal has the same heat treat-ment characteristics as the base

  Tool, Steel, Welding, Welding of tool steel, Tool steel welding

Retain your edge - Uddeholm

Classifi ed according to EU Directive 1999/45/EC. For further information see our “Material Safety Data Sheets”. Edition 2, 05.2012. The latest revised edition of this …

HEAT TREATMENT OF TOOL STEEL - Uddeholm Global

austenite. After one tempering at a high tem-perature the microstructure consists of tempered martensite, newly formed martensite, some retained austenite and carbides. Hardness Tempering temperature A = martensite tempering B = carbide precipitation C = transformation of retained austenite to martensite D = tempering diagram for high speed steel

  Transformation, Austenite

Uddeholm Mirrax 40

Uddeholm Mirrax 40 6 FURTHER INFORMATION Please contact your local Uddeholm office for further information on the selection, heat treatment and application of Uddeholm tool

  Treatment, Heat, Tool, Uddeholm, Heat treatment, Uddeholm tool

Uddeholm Sverker 21

Uddeholm Sverker 21 3 Uddeholm Sverker® 21 THE BACKBONE OF COLD WORK TOOLING The steel grade was developed around 1930 and is still going strong. Ledeburitic 12 % Cr-steel are still the most commonly used tool steel

  Steel, Sverker 21, Sverker, 174 21

UDDEHOLM TOOL STEELS FOR PLASTIC MOULDING

UDDEHOLM TOOL STEELS FOR PLASTIC MOULDING. ... Edition 12, 03.2016 ... Mouldmaking 10 Moulding 14 Moulding methods – Injection moulding 17 – Compression moulding 17 – Blow moulding 18 – Extrusion 18 The same quality and service available worldwide 20 …

  Edition, Tool, Steel, Plastics, Injection, Blow, Moulding, Uddeholm, Uddeholm tool steels for plastic moulding

UDDEHOLM DIEVAR

7 UDDEHOLM DIEVAR * Depth of case = distance from surface where hardness is 50 HV 0.2 over base hardness Dimensional changes during hardening and tempering During hardening and tempering the tool is

  Tool, Uddeholm, Viread, Uddeholm dievar

UDDEHOLM STAVAX ESR

Retained austenite % 14 12 10 8 6 4 2 Retained Holding time austenite 20 min. Holding time 60 min. 1050°C 1020°C Retained austenite 1030°C Quenching media • Fluidized bed or salt bath at 250–550°C (480–1020°F), then cool in air blast •Vacuum with sufficient positive pressure

  Austenite, Detainer, Retained austenite

Uddeholm Vanadis 8 SuperClean - edelstahl-schweiz.ch

Uddeholm Vanadis 8 SuperClean 4 BEARBEITBARKEIT Ungefähre Bearbeitbarkeit für Uddeholm Stähle Vanadis 10 SuperClean, Vanadis 8 SuperClean, Vanadis 23 SuperClean und

  Uddeholm, Vanadis, Superclean, Superclean 4, Uddeholm vanadis

109237-Ramada Improving Together Bch Mio

classe famÍlia marca perfis disponÍveis normas composiÇÃo quÍmica % euronorm aisi une din w.nr.º cs im n cr mo ni vw outros aÇos rÁpidos 0 104 vanadis 23 • *

  Vanadis

DIEVAR - ASSAB

3 23Diev DIEVAR Dievar is a hot work die steel specially developed by Uddeholm Tooling, our steel mill in Sweden, to provide the best possible performance.

  Uddeholm, Viread, Dievar dievar

ASSAB Tool Steel Performance Comparison Chart

ASSAB Tool Steel Performance Comparison Chart ( ) - modified grade www.assab.com This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses.

  Chart, Performance, Comparison, Tool, Steel, Assab, Assab tool steel performance comparison chart

STAVAX ESR - assab-japan.com

4 | STAVAX ESR 特性 物性値 熱処理 軟化焼鈍 脱炭を防ぐため材料の表面を保護し，890oCに加 熱します。その後850 oCまで毎時20oC，700 Cまで毎 時10oCの冷却速度での冷却速度で炉内冷却し，そ の後，大気 …