1 Toll Free (800) 955-4637 (661) 321-0447 Fax (661) 321-0449321 Industrial St. Bakersfield, CA 93307 PropertyTest MethodCERTIFIED PROPERTIEST hickness (mils nominal)ASTM 51991020304060 Thickness, ".019".0285".038".057"Min. Tensile Properties 1. Strength at BreakASTM D882, Min (MD & TD)24 lbs/in. 2. Elongation at Break (%)ASTM D882250%360%380%430%450% 3. Modulus @ 100% ElongationASTM D88210 Strength (min. average lbs)ASTM D StabilityASTM D1204, Max Chg (MD & TD)4%4%3%3%3%Low Temperature ImpactASTM D1790, Pass-10 F-15 F-20 F-20 F-20 FINDEX PROPERTIESS pecific GravityASTM D792, Extraction (Max. % wt loss)ASTM Plasticizer Molecular WeightASTM D2124400400400400400 Volatile Loss (Max % wt loss)ASTM to Soil Burial (% max in original value) 1. Breaking FactorASTM G1605%5%5%5%5% 2. Elongation at Break (%)ASTM G16020%20%20%20%20% 3.
2 Modulus (Force) @ 100% ElongationASTM G16020%20%20%20%20%Hydrostatic Resistance ( min)ASTM D75142 psi68 psi100 psi120 psi180 psiSEAM REQUIREMENTSF actory Seaming MethodDielectric Fusion WeldShear Strength (lbs/in min)ASTM D308320 lbs/in116 lbs/inPeel Adhesion (lbs/in min)ASTM D41310 lbs/in15 lbs/in15 lbs/in15 lbs/inPolyvinyl Chloride (PVC)ValuesSPECIFICATION SHEETAll information, recommendations and suggestions appearing in this literature concerning the use of our products are based upon test and data believed to be reliable; however, it isthe user's responsibility to determine the suitability for their own use of the products described herein. Since the actual use by others is beyond ourcontrol, no guarantee orwarrantyof any kind, expressed or implied, is made by AccuGeo Liner , Inc. as to the effects of such use or the results to be obtained, nor does AccuGeo Liner , Inc.
3 Assume anyliability in connection herewith. Any Statement made herein may not be absolutely complete since additional information may be necessary or desirable when particular orexceptional conditions or circumstances exist or because of applicable laws or government regulations. Nothing herein contained is to be construedas permission or as arecommendation to infringe any patent.