Carbothane 134 HG - CARBOLINE

1 Carbothane 134 HG. Selection & Specification data Surface & Substrate preparation Generic Type Aliphatic Acrylic Polyurethane Surfaces must be clean and dry. Employ adequate methods to remove dirt, dust, oil and General all other contaminants that could interfere Description Thin film, high gloss finish with with adhesion of the coating. exceptional weathering performance characteristics. Used extensively in Steel SIS SA2 with a surface profile of 25 50 for virtually all industrial markets, 134 HG maximum protection. provides a smooth, durable finish that has SIS ST2 or ST3 as minimum requirement. Prime superior resistance to corrosion, with specific CARBOLINE primers defined in abrasion and chemical exposure. Market Guides or as recommended by your CARBOLINE representative. Refer to the specific primer's Product Data Sheet for detailed Features High solids, low VOC content Thin-film, requirements of the specified primer.

2 Single coat protection. Excellent weatherability Galvanized Steel SSPC-SP1 and prime with specific CARBOLINE Excellent flow characteristics allow primers defined in Market Guides or as r for application by spray or roller recommended by your CARBOLINE representative. Superior impact and abrasion resistance Refer to the specific primer's Product Data VOC compliant to current EPA 1990 Sheet for detailed requirements of the specified PG6/23(97) primer. Colour BS 4800 & RAL Aluminium SSPC-SP1 and prime with specific CARBOLINE primers defined in Market Guides or as recommended by your CARBOLINE representative. Finish Gloss Refer to the specific primer's Product Data Sheet for detailed requirements of the specified Primers Refer to Substrates & Surface primer. Preparation Previously Lightly sand or abrade to roughen and degloss Topcoats Carbothane 134 HG Clear Coat when Painted Surfaces the surface.

3 Existing paint must attain a minimum 3B rating in accordance with ASTM D3359. required X-Scribe adhesion test. Prime with specific CARBOLINE primers defined in Market Guides or as DFT 50-62 recommended by your CARBOLINE representative. Refer to the specific primer's Product Data Sheet for detailed requirements of the specified Solids By Volume: 70% 2% primer. Content Theoretical m2/l at 25 Performance Data Coverage Rate Allow for loss in mixing and application Test Method System Results Report #. VOC Values As supplied: 264 g/l Blasted Steel ASTM D4541 2562 psi 1 ct. Epoxy 09360. Adhesion (Pneumatic). These are nominal values and may vary 1 ct. 134 HG. Blasted Steel slightly with colour. ASTM D3359. 1 ct. Epoxy 5A 09360. Adhesion 1 ct. 134 HG. Dry Temp. Continuous: 93 C 70 mg. loss after 1000. Resistance Non-Continuous: 121 C ASTM D4060.

4 1 ct. 134 HG cycles, CS17 wheel, 09360. Abrasion Discoloration and loss of gloss is 1000 gm. load observed above 93 C. No blistering, rusting Blasted Steel or cracking; gloss Thinner Spray # 214 ASTM G26 1 ct. Epoxy retention of 85%;. Weatherometer 1 ct. 134 HG colour change of 1 09360. Brush/Roller # 215 McAdam unit after 2000 hours. Cleaner #2 ASTM G53 Blasted Steel No rusting, blistering ASTM D4587 1 ct. Org. Zinc or loss of adhesion;. 03390. Accelerated 1 ct. Epoxy less than 5% gloss Weathering 1 ct. 134 HG loss after 3000 hours No rusting, blistering, Blasted Steel loss of bond or any 1 ct. Org. Zinc ASTM B117 measurable creepage 03390. 1 ct. Epoxy Salt Fog from the scribe after 1 ct. 134 HG. 3000 hours. Blasted Steel ASTM D3363. 1 ct. Epoxy H 09360. Hardness 1 ct. 134 HG. ASTM D2794 155 inch-pounds; no Impact 1 ct. 134 HG visible cracking.

5 Gard- 03259. Resistance ner Impact Tester No rusting in the ASTM D870 scribe; no blistering, Immersion Blasted Steel softening or 03390. Resistance 1 ct. Org. Zinc discoloration after 1 ct. Epoxy either 30 days of fresh- 1 ct. 134 HG water immersion or 30. days of salt water immersion at 75 F. January 2004. To the best of our knowledge the technical data contained herein is true and accurate on the date of publication and is subject to change without prior notice. User must contact CARBOLINE Company to verify correctness before specifying or ordering. No guarantee of accuracy is given or implied. We guarantee our products to conform to CARBOLINE quality control. We assume no responsibility for coverage, performance or injuries resulting from use. Liability, if any, is limited to replacement of products. NO OTHER WARRANTY OR GUARANTEE OF ANY KIND IS MADE.

6 BY CARBOLINE , EXPRESS OR IMPLIED, STATUTORY, BY OPERATION OF LAW, OR OTHERWISE, INCLUDING MERCHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE. CARBOLINE and Carboguard are registered trademarks of CARBOLINE Company. Application Equipment Application Conditions Spray Applica- This is a high solids coating and may require Condition Material Surface Ambient Humidity tion (General) adjustments in spray techniques. Wet film thickness is easily and quickly achieved. The Normal 16 -29 C 18 -29 C 18 -29 C 40-60%. following spray equipment has been found suitable and is available from manufacturers Minimum 10 C 2 C 2 C 10%. such as Binks, DeVilbiss and Graco. Maximum 38 C 49 C 35 C 80%. Conventional Pressure pot equipped with dual regulators, Spray 3/8 minimum material hose, .070 fluid tip Industry standards are for substrate temperatures to be above and appropriate air cap.

7 3 C the dew point. Caution: This Product is moisture sensitive in the liquid stage and Airless Spray Pump Ratio: 30:1 (min.) until fully cured. Protect from high humidity, dew and direct GPM Output: (min.) moisture contact until fully cured. Application and/or curing Material Hose:3/8 (min.) in humidity's above maximum, or exposure to moisture from rain or Tip Size: . dew may result in a loss of gloss and/or micro bubbling of the Output PSI: 2100-2400 product. Filter Size: 60 mesh Teflon packings are recommended and available from the pump manufacturer. Curing Schedule Brush & Roller Multiple coats may be required to obtain desired (General) appearance, recommended dry film thickness and Surface adequate hiding. Avoid excessive re-brushing or Temp. & 50% Dry to Handle Dry to Recoat Final Cure re-rolling. For best results, tie-in within 10.

8 Minutes @ 24 C. Relative Humidity Brush Recommended for touch-up only. Use a medium, 2 C 36 Hours 36 Hours 14 Days natural bristle brush. 10 C 16 Hours 16 Hours 10 Days 24 C 8 Hours 8 Hours 7 Days Roller Use a short-nap mohair roller cover with phenolic core. 32 C 4 Hours 4 Hours 5 Days These times are based on a 50 dry film thickness. Higher film Mixing and Thinning thickness, insufficient ventilation or cooler temperatures will require longer cure times and could result in solvent entrapment and premature failure. Mixing Power mix Part A separately, then combine and power mix. DO NOT MIX PARTIAL KITS. Packaging, Handling & Storage Ratio 4:1 Ratio (A to B). Thinning Spray: Up to 20% w/ #214 Pack Size 5 Litre :10 Litre Brush: Up to 20% w/ #215. Roller: Up to 20% w/ #215. Use of thinners other than those supplied or Flash Point (Setaflash) Part A: 10 C.

9 Recommended by CARBOLINE may adversely affect Part B: 41 C. product performance and void product warranty, whether expressed or implied. Storage (General) Store Indoors. Pot Life 4 Hours @ 24 C and less at higher temperatures. Storage Temperature 4 -43 C. Pot life ends when coating becomes too viscous & Humidity 0-80% Relative Humidity to use. MOISTURE CONTAMINATION WILL. SHORTEN POT LIFE AND CAUSE GELLATION. Shelf Life 24 months @ 24 C. Cleanup and Safety Cleanup Use #2 Thinner. In case of spillage, absorb and dispose of in accordance with local applicable regulations. Safety Read and follow all caution statements on this product data sheet and on the MSDS for this product. Employ normal workmanlike safety precautions. Hypersensitive persons should wear protective clothing, gloves and use protective cream on face, hands and all exposed areas.

10 Ventilation When used in enclosed areas, thorough air circulation must be used during and after application until the coating is cured. The ventilation system should be capable of preventing the solvent vapour concentration from reaching the lower explosion limit for the solvents used. User should test and monitor exposure levels to insure all personnel are Portobello Industrial Estate below guidelines. If not sure or if not able to Birtley monitor levels, Use MSHA / NIOSH approved supplied air respirator. Chester le-Street County Durham Caution This product contains flammable solvents. Keep DH3 2RE. away from sparks and open flames. All electrical equipment and installations should be made and grounded in accordance with the Tel: +44 191 411 3133. National Electric Code. In areas where Fax: +44 191 411 3132. explosion hazards exist, workmen should be required to use non-ferrous tools and wear conductive and non-sparking shoes.