CCW MiraDRI 860/861 - The Cade Corporation

1 CCW MiraDRI 860/861 . SHEET MEMBRANE. WATERPROOFING SYSTEMS. DESCRIPTION WARNINGS AND HAZARDS. CCW MiraDRI 860/861 are self-adhering sheet membranes CCW-702 and CCW-704 contain flammable and com- consisting of 56 mils ( mm) of rubberized asphalt lami- bustible solvents. Avoid exposure to open flame. Avoid nated to 4 mils ( mm) of polyethylene to form a mini- breathing vapors. Use only in areas with adequate venti- mum 60 mil ( mm) membrane. CCW MiraDRI 860 mem- lation. Refer to MSDS for important warnings and prod- brane is a summer grade material, suitable for installa- uct information. tions where the ambient temperature is 40 F ( C) or TECHNICAL DATA. above.

2 CCW MiraDRI 861should be used for applica- PROPERTY TEST METHOD RESULTS. tions between 25 F ( C) and 65 F (18 C). The combi- Color - Dark Gray nation of these two excellent waterproofing materials pro- vides a high-performance, extremely durable waterproof- Thickness ASTM D 3767 60 mils ing barrier. Tensile (Membrane) ASTM D 412 325 psi Tensile (Film) ASTM D 882 5000 psi TYPICAL USE. Elongation ASTM D 412 350%. CCW MiraDRI 860/861 membranes are used for vertical Permeance ASTM E 96 perms and horizontal waterproofing on structural foundation walls and decks. Below-grade foundation walls, tunnels, split Low Temp. Flexibility ASTM D 1970 Unaffected @ -45oF. slabs, plaza decks and parking decks are all areas where Crack Cycling*.

3 (100 cycles) ASTM C 836 Unaffected @ -25oF. CCW MiraDRI 860/861 may be applied. CCW MiraDRI . 860/861 also may be used in interior areas such as me- Peel Strength ASTM D 903 lb/in. chanical rooms, laboratories, kitchens and bathrooms. Lap Adhesion ASTM D 1876 lb/in. CCW MiraDRI 860/861 should be covered with either CCW Puncture Resistance ASTM E 154 60 lb. (min). 200V/300HV Protection Course, CCW Protection Board, Soil Burial GSA-PBS 07121 16 wks, no effect or CCW MiraDRAIN drainage composites. H2O Absorption ASTM D 570 by wt. LIMITATIONS Hydrostatic head ASTM D 751 230 ft. Do not apply where membrane will be subject to * 180 bend over a 1" (25mm) mandrel at -45 F (-43 C).

4 Continuous exposure to sunlight. Do not apply primer or membrane to frozen concrete. PACKAGING. Optimum results are obtained when membrane is CCW MiraDRI 860/861 -36 = 36" wide X 67' roll (200 ft2). installed at temperatures above 25 oF. Between 25oF. 25 rolls per pallet (5000 ft2) - Weight = 80 lb/roll (approx.). and 65oF use the CCW MiraDRI 861 membrane. CCW. MiraDRI 860 can be used from 40oF and above. Other membrane thicknesses and configurations are available by special order. Do not apply primer or membrane to a damp, frosty or contaminated surface. CCW-702 VOC Compliant Solvent Based Primer: 5 gallon pails (45 pails per pallet). Not recommended as a pond or tank liner except for between slab applications.

5 CCW-714 Water Base Primer: 1 gallon pails (100 pails per pallet). Do not apply over sealants containing coal tar or polysulfides. In the event of existing bitumen modified CCW-AWP Water Base Primer: materials, consult your Carlisle representative. 1 gallon pails (100 pails per pallet). 5 gallon pails (45 pails per pallet). APPLICABLE STANDARDS CCW-715 Damp Concrete Primer: CCW MiraDRI 860/861 meets the applicable requirements 5 gallon pails (45 pails per pallet). of: CCW-704 Mastic and CCW LM-800XL: GSA; PBS PCD 07121 30 oz. Qt. Tube (12 tubes per carton), 5 gallon pails (45 pails per pallet). USN; NAVFAC TS-07111. INSTALLATION. VA; H-08-1. Federal Construction Guide Specs; FCGS-07111 Weather Conditions Corps of Engineers; CEGS-07111-3-82 CCW MiraDRI 860 is used for applications where the sur- face temperatures is 40 F.

6 ( C.) and above. CCW. UL 790, Class A. MiraDRI 861is used for applications where the surface temperature is between 25 F ( C.)and 65 F (18 C). Do not apply CCW MiraDRI 860/861 to frozen or wet sub- the membrane against the substrate while pulling the re- strates. The membrane should not be left exposed to di- lease paper free. Install membrane with side laps over- rect sunlight for longer that 14 days. lapped a mini mum of " (63mm) and end laps a mini- Substrate Preparation: CCW MiraDRI 860/861 can be mum of 5"(127mm). Carlisle Coatings & Waterproofing applied to concrete, metal, wood, insulated wall systems recommends that the membrane be rolled in place im- or masonry surfaces.

7 All substrates must be clean,dry mediately after its placement to ensure full adhesion to and free of surface irregularities. the primed substrate. Apply a bead of CCW-704 Mastic OR CCW-703V Liquiseal at terminations and cut edges, Concrete Substrates: Structural concrete must be cured joints, drains, penetrations and protrusions. For walls over a minimum of 7 days and lightweight structural concrete 8' (240cm), the membrane should be placed in lifts. Pro- must cure a minimum of 14 days before the application of tect the CCW MiraDRI 860/861 membrane with the appro- CCW MiraDRI 860/861 . Repair surfaces that are not struc- priate CCW MiraDRAIN drainage composite, CCW 200V/.

8 Turally sound, have voids, protrusions,rough spalled ar- 300HV Protection Course or CCW Protection Board V. eas, loose aggregate or exposed course aggregate. Void areas should be filled with latex Portland cement, con- HORIZONTAL INSTALLATION. crete or epoxy concrete and troweled smooth to match Start at the low point (establish a starting point with a the existing surface. Protrusions and other rough areas chalk line if necessary) and work towards the high point should be broken off and patched as above. CCW LM- in shingle fashion. Remove 2' to 3' (60cm to 90cm) of the 800XL or CCW-201 may be used to fill small voids, hon- release paper and apply the membrane to the substrate.

9 Eycombs or bug holes. Continue pulling the release paper free while pressing and Masonry Substrate: Rough masonry may require the smoothing the membrane against the substrate. Apply in surface to be parged with a plaster coat of cementitious a straight line avoiding wrinkles and over correcting. Roll material to form a well adhered, smooth and uniform fin- the membrane with a minimum 75 lb. (34kg) linoleum ish. Allow the parge coat to dry before priming and install- roller. Install membrane with side laps overlapped a mini- ing the CCW MiraDRI 860/861 waterproofing membrane. mum of " (63mm) and end laps a minimum of 5"(127mm). Apply a bead of CCW-704 Mastic at all ter- Chemical Additives: Curing compounds should be a minations of the membrane and T joints.

10 Apply a 3/4". clear resin-based material without waxes, oils or pigments. (18mm) fillet of CCW LM-800XL or CCW-201 in all inside Form release agents must not transfer tothe concrete. corners of planter boxes, shower stalls and shower pans Curing compounds or form release agents that adversely applications. Patch inadequately lapped seams and dam- affect the adherence of the CCW MiraDRI 860/861 water- aged areas with CCW MiraDRI 860/861membrane cover- proofing membrane must be removed from the substrate ing the damaged area by a minimum of 6" (150mm). Fish- prior to application. mouths and severe wrinkles should be slit, flaps over- Priming and Detailing: All concrete, metal and masonry lapped and repaired as above.