Transcription of Corning® Gorilla® Glass 6
1 Corning gorilla Glass 6 Corning gorilla Glass 6 is engineered to better survive drops from the worldwide average height. In lab tests, it successfully survives up to drops onto rough surfaces, while still maintaining the superior scratch performance synonymous with gorilla Glass . At meters, alternative aluminosilicate and soda lime glasses didn t survive a single drop. gorilla Glass 6 has up to 2x improvement in scratch performance compared to alternative ts Improved drop performance, up to resistance to scratch and sharp contact damageHigh retained strength after useSuperior surface quality Viscosity Softeni ng Point ( poises)885 CAnnealing Point ( poises)624 CStrain Point (1 poises)572 C Properties Density Young s Modulus 77 GPaPoisson s Ratio Modulus GPaVickers Hardness (200g load) Unstrengthened 611 kgf/mm2 Strengthened 678 kgf/mm2 Fracture Toughness MPa Coe cient of Expansion (0-300 C)
2 X 10-7/ CProduct InformationApplications Ideal protective cover material for the front and back of all electronic devices: Smartphones Notebook PCs Tablets Smartwatches and wearables Smart Home devices Cameras Commercial and Point of Sale Displays Thickness mm mmChemical Strengthening Please contact a Corning Account Manager for chemical strengthening capability based on thickness and application. Optical Refractive Index* (590 nm) Core Compression Layer Photo-elastic constant nm/cm/MPa Transmission @ mm thickness2004006008001000120014001600180 02000220024001009080706050403020100 Wavelength (nm)% TransmittanceCorning gorilla Glass 6 Transmittance 2000*Refractive index is used for FSM-based measurements since it is una ected by ion-exchange Durability Durability is measured via weight loss per surface area afterimmersion in the solvents shown below.
3 Values are highly dependent upon actual testing conditions. Reagent Time Temperature Weight Loss ( C) (mg/cm2) HCI 5% 24 hrs. 95 :HF 10% 20 min. 20 10% 20 min. 20 5% 6 hrs. 95 Electrical TangentDielectric ConstantFrequency (MHz)Terminated coaxial line similar to that outlined in NIST Technical Notes 1520 and ipsumContact gorilla Glass 6 Corning and gorilla are a registered trademarks of Corning Incorporated, Corning, , USA 2020 Corning Incorporated. All rights : 08102020 Always Tough. Always Test PerformanceScratch Test PerformanceCompetitive Al-SiGorilla Glass Drop on 180 grit Sandpaper with Corning Puck, GlassNormalized Average Height to Failure (m) Glass 5We tested for scratch threshold using our Knoop Diamond Scratch Test.
4 Competitive Al-Si(4 Newton Load) gorilla Glass 5(4 Newton Load) gorilla Glass 6(4 Newton Load)