Transcription of Corning® Gorilla® Glass Victus™
1 Corning gorilla Glass Victus Toughest gorilla Glass yet; Corning gorilla Glass Victus signi cantly improves both drop and scratch performance for the rst time ever in the gorilla Glass family, addressing consumer demand for improved durability. Bene ts Improved drop performance, up to 2 m High resistance to scratch and sharp contact damage High retained strength after use Superior surface quality Lower softening point vs. Corning gorilla Glass 5 and Corning gorilla Glass 6 Applications Ideal protective cover material for the front and back of all electronic devices: Smartphones Notebook PCs Tablets Smartwatches and wearables Smart Home devices Cameras Commercial and Point of Sale Displays Viscosity Softeni ng Point ( poises)827 CAnnealing Point ( poises)591 CStrain Point (1 poises)543 C Chemical Durability Durability is measured via weight loss per surface area afterimmersion in the solvents shown below.
2 Values are highly dependent upon actual testing conditions. Reagent Time Temperature Weight Loss ( C) (mg/cm2) HCI 5% 24 hrs. 95 :HF 10% 20 min. 20 10% 20 min. 20 5% 6 hrs. 95 PropertiesDensity g/cm3 Young s Modulus 77 GPaPoisson s Ratio Modulus GPaVickers Hardness (200g load) Unstrengthened 590 kgf/mm2 Strengthened 651 kgf/mm2 Fracture Toughness MPa Coe cient of Thermal Expansion (0-300 C) x 10-7/ CChemical Strengthening Please contact a Corning Account Manager for chemical strengthening capability based on thickness and application. Product InformationThickness mm mmAvailable upon requestElectrical TangentDielectric ConstantFrequency (MHz)Terminated coaxial line similar to that outlined in NIST Technical Notes 1520 and Refractive Index (590 nm) Core Glass * Compression Layer Photo-elastic constant nm/cm/MPa Transmission @ mm thicknessCorning gorilla Glass Victus Transmittance 2000*Core index is used for FSM-based measurements since it is una ected by ion-exchange gorilla Glass Victus Always Tough.
3 Always Innovating. Corning is a registered trademark of Corning Incorporated, Corning, , USA 2020 Corning Incorporated. All rights Test PerformanceScratch Test PerformanceThe typical threshold for competitive aluminosilicate is at 2-4 Newtons. #TougherTogetherGorilla Glass Victus Competitive Drop on 180 grit Sandpaper with Corning Puck, GlassHeight to Failure (m) gorilla Glass Victus (8 Newton Load)Alternative Al-Si (4N) gorilla Glass 5 (4N) gorilla Glass Vict us (8N) gorilla Glass 6 (4N)Competitive Al-Si(4 Newton Load)Alternative Al-Si (4N) gorilla Glass 5 (4N) gorilla Glass Vict us (8N) gorilla Glass 6 (4N)We tested for scratch threshold using our Knoop Diamond Scratch Test. For gorilla Glass Victus , the scratch threshold is typically at 7-10 Newtons. That s up to 4x better!In lab tests, gorilla Glass Victus survived drops from up to 2 meters.
4 Competitive aluminosilicate typically fails from less than meters.