EPOXY BACKING GROUT epigen 0301

1 A tough infusible solvent free advanced composite systemdeveloped to be used as a multipurpose high strengthcasting and grouting polymer. Exhibits excellent chemicalresistance, corrosion resistance, and high structuralintegrity under stress in both compression and product is designed to be used effectively in hot orcold climates, and is able to be blended with gradedaggregate without appreciable loss of strength. Addition ofgraded aggregate is recommended when installationdepth is extreme or to control excessive exotherm underhot for use on a variety of surfaces including steel,wood, and APPLICATIONSC ivils Foundation BeddingSlipway FoundationsRoad Bridges GroutingBedding RailsCrusher BACKING & GroutingFloor Re LevellingConcrete RepairHigh Strength AdhesiveCasting Mould MakingChemical AnchoringPrecision GroutingEngineering GroutCrack RepairWet to Dry ConcreteEPOXY BACKING GROUT epigen 0301 FEATURESE ngineered for high mechanical strengthExtremely strong adhesiveBroad spectrum chemical resistanceCures in 6 hoursFree of all solvents - zero VOCC ures even when applied under cold adverse conditionsSuitable for underwater usePROFILER atio by weight10 parts Component A 1 part Component B Pot Life minutes @ 24oC30 Mixed consistency @ 24oCFlowable LiquidSpecific gravity when CURED PROPERTIESC ompressive strength ASTM D695.

2 Mpa>100 Compressive strength after 24 hours, Mpa>88 Tensile strength ASTM D638, Mpa>21 Flexural strength ASTM D638, Mpa>21 Hardness, Shore D90 Comp Modulus of Elasticity ASTM D695, Mpa>1300 Comp Modulus of Elasticity after 24 hours, Mpa>770 Elongation of thermal expansion ASTM (cm/cm/o C) x 10-5 Dielectric constant ASTM D150 (150 KHz) exposure temperature, o C130 Heat deflection temperature ASTM D648, o C75 Cure time @ 20mm, Minutes90 Cure time to open service @ 20mm, Hours4 Ultimate cure time @ 20mm, Hours48 This information is supplied as an indicative reference should be used where direct comparisons are to be UNDER LOADASTM D621-64 Method AEpigen 301 resin was mixed with equal parts by weight,of 16/30 Silica distinct applied stresses and temperatures weremaintained, consistent with Western Power directivesfor loading evaluation for equipment grouting & StressTemperatureDeformation15 Mpa40 PREPARATIONM ethods for substrate preparation preference using highpressure water blasting, or mechanical techniques such asgrinding or advice is available to ensure suitable preparationprocedure is employed for specific of product should be carried out using slow speedmixers and carried out by adding component B to thecomponent A.

3 Once uniform in colour, mixed productshould be poured directly into the area requiring treatment orapplied to surfaces nominated for service. In underwaterservice, any water within the void will be displaced filling large cavities, epigen 301 may be bulk filledwith equal parts by weight 16/30 mesh Silica Sand to reducethe amount of resin used. This is seen as an advantageparticularly with high ambient temperature since the additionof aggregate reduces the exotherm and any resultant postcure contraction. The addition at the recommended rate willretain strength and pourability features. The kits have beendesigned for equal parts aggregate addition by simplytopping up the mixed product container with silica in cure may arise due to the amount of materialbeing applied, the thickness of material being applied, thesurface temperature, and the product temperature. Thecure may be increased by heating product or by leavingmixed material stand for 15 minutes before use.

4 The curemay be decreased by cooling the product before :2003/Aprrev08,2011/NovEPOXY BACKING GROUT epigen 0301 FORMWORKIn grouting applications, waxed timber, acrylic sheet, mildsteel or galvanised forms have also be used with joins using silicon at 21oC. Samples cured for 10 days at = Continuous or long term immersion2=Short term immersion3=Splash and spills4=Avoid contactAcetic Acid, 10 %2 Ammonium Chloride1 Hydrochloric Acid, 5 %1 Beer1 Hydrochloric Acid, 10 %1 Dichloromethane4 Hydrochloric Acid, conc2 Diesel Fuel1 Nitric Acid, 10 %2 Kerosene1 Phosphoric Acid, 5 %1 Petrol1 Phosphoric Acid, 20 %2 Salt Water1 Sulfuric Acid, 5 %2 Sewage1 Sulfuric Acid, 20 %3 Skydrol1 Ammonium Hydroxide, 5 %1 Sodium Cyanide1 Ammonium Hydroxide, 20 %1 Sodium Hypochlorite1 Potassium Hydroxide, 5 %1 Toluene2 Potassium Hydroxide, 20 %1 Trichloroethane2 Sodium Hydroxide, 5 %1 Wine1 Sodium Hydroxide, 20 %1 Xylene1 CHEMICAL RESISTANCEThe following results represent relevance when in groutingapplications of chemical information is supplied as an indicative reference should be used where direct comparisons are to be GUIDEAs kg of epigen 301 / kg of epigen 301 / 10 kg of epigen 301 / m @ with equal parts by weight 16/30 Silica kg of epigen 301 + kg of aggregate / kg of epigen 301 + 10 kg of aggregate / 10 kg of epigen 301 + 10 kg of aggregate / m @ PRODUCTSMANUFACTURED BYPeerless Industrial Systems Pty LtdABN 14 097 615 39179 Robinson Ave, Belmont, WA 6104PO Box 407, Cloverdale, WA 6985 Phone: (08) 9477 3788 Fax: (08) 9477 3766 Email.