Formulating High-Performance Waterborne Epoxy Coatings

1 Formulating High-Performance Waterborne Epoxy Coatings September 11-12, 2006. Authors: Michael J. Watkins, Daniel J. Weinmann, and Jim D. Elmore Affiliation: Hexion Specialty Chemicals, Inc. Presenter: Michael J. Watkins Senior Staff Research Scientist Hexion Specialty Chemicals, Inc. Westhollow Technology Center, 3333 Highway 6 South Houston, Texas 77082. Phone: 832-486-6677. Email: Presented at a meeting of the Thermoset Resin Formulators Association at the Hyatt Regency Montreal in Montr al, Qu bec, Canada, September 11-12, 2006.

2 This paper is presented by invitation of the TRFA. It is publicly distributed upon request by the TFRA to assist in the communication of information and viewpoints relevant to the thermoset industry. The paper and its contents have not been reviewed or evaluated by the TFRA and should not be construed as having been adopted or endorsed by the TFRA. Formulating High-Performance Waterborne Epoxy Coatings Abstract This paper deals with two myths. The first is that Waterborne Epoxy Coatings cannot achieve the performance of solvent-based Epoxy Coatings .

3 The second myth is that coating formulators often believe that they can formulate Waterborne Epoxy Coatings just like they do other Waterborne systems. In fact, the tools required to formulate Waterborne Epoxy Coatings can be fairly unique and very specific. Experience has shown that formulators, who deviate from these specific tools, often achieve poor coating performance . This paper discusses the many preferred approaches and specific recommendations to formulate truly high performance Waterborne Epoxy Coatings .

4 Important Note Normally, the authors would prefer to present this paper by providing general Formulating concepts, with a minimum of specific material references. However, we have repeatedly found that, without very specific material recommendations, formulators are often unsuccessful in Formulating High-Performance Waterborne Epoxy Coatings . They unknowingly select pigments, additives, etc., which may give great performance in other Coatings , but which give sub-optimal performance in these Waterborne Epoxy Coatings .

5 This reinforces the myth that High-Performance Waterborne Epoxy Coatings cannot be formulated. We have structured this paper to emphasize preferred Formulating concepts, and to identify specific materials (pigments, fillers, additives, etc.) which we or others have found to work well in high - performance systems. We do this with the understanding that the materials which we cite are probably not the only ones that will give high performance Coatings . However, at this time, these are the only ones that we are aware that do so.

6 We trust that the readers of this paper will be able to use this information constructively, and may well find alternative materials which will also give High-Performance Coatings . Background Epoxy resins (based on the diglycidyl ether of bisphenol A) were commercialized nearly 60 years ago. It was quickly determined that they are useful in Formulating direct-to- metal Coatings with excellent adhesion, chemical resistance, and corrosion resistance. As such, Epoxy based Coatings have been used extensively as High-Performance primers for metal substrates.

7 As an example, virtually every automobile manufactured in the world today is first coated with an Epoxy based primer which provides outstanding corrosion resistance. The most widely used Epoxy resins, by far, are still those based on bisphenol A. Historically, most High-Performance Epoxy primers, especially those used in ambient cure applications, are based on solvent based Epoxy resins. So, although they provide excellent performance , they have the disadvantage of relatively high VOC content. About 30 years ago, chemists began Formulating Waterborne Epoxy resins and curing agents which could be formulated at significantly lower VOC levels than solvent based Epoxy Coatings .

8 The technical problem which arises is that bisphenol A Epoxy resins are rather hydrophobic, and do not readily disperse in water. Therefore, surfactants were developed which would disperse these hydrophobic resins in water. The first Thermoset Resin Formulators Association 2006 Annual Meeting September 11-12, Montr al, Qu bec, Canada 2. Formulating High-Performance Waterborne Epoxy Coatings generation (Type 1) Waterborne Epoxy resins are liquid Epoxy resins dispersed in water using appropriate surfactants.

9 Curing agents are generally water soluble amines. Often the curing agents are salted with an acid to enhance water solubility. The use of surfactants and water soluble amines result in coating films which are relatively hydrophilic. As such, they do not provide good corrosion resistance when applied to metallic substrates. However, they are very useful when applied to non-metallic substrates, such as flooring or masonry. The weakness of their poor hydrophobicity is not evident in these applications.

10 Coatings formulated with these materials can approach 0 VOC. The next generation (Type 2) Waterborne resins are dispersions of solid Epoxy resins in water. These generally require the use of cosolvents as coalescing aids in the film formation process, so very low VOC levels are not achievable. Water soluble amines are generally used as curing agents. The performance of the Type 2 system is improved over Type 1. This is due largely to lower curing agent demand by the higher molecular weight solid resin.