Heat Treated Steel Plate - C.W. Carry

1 heat Treated Steel PlateThe industry standard for high strength and abrasion resistanceEssar Steel Algoma is dedicated to being North America s leading supplier of hot rolled sheet and Plate products through continuing innovation and improvement of our products, processes and people. Our mission is to deliver quality products that meet or exceed our customers expectations and support their success in the markets they Plate . The industry standard for high strength and abrasion resistanceEssar Steel Algoma a manufacturing capacity of million tons per year, Algoma s size and diverse capabilities enable us to deliver responsive, customer driven product solutions straight from the ladle to direct applications in the automotive, construction, energy, manufacturing, pipe and tube and Steel distribution industries.

2 Situated at the hub of the Great Lakes, our strategic geographic location offers customers a logistical advantage with fast, direct shipping via rail, truck and marine throughout North s heat Treated Plate facility provides a full range of high quality heat Treated products for high strength, abrasion resistant , ballistic and other specialty Plate applications. Our lean chemistries and unique water quenching procedures result in excellent notch toughness, through thickness hardness, superior flatness, outstanding surface quality, and easy company s spirit and focus is reflected in our commitment to pursue a strategy that balances the optimal mix of products, markets, assets, and culture.

3 We are an entrepreneurial company with the skills, expertise and growing capability to meet the industry s challenges head on. Our perspective is responsive, nimble and open to unconventional approaches. Strong customer service backed by superior performance will demonstrate to all of our stakeholders customers, investors and employees that Essar Steel Algoma is a different kind of Steel Steel Algoma is one of the world s key suppliers of heat - Treated Plate for highstrength, abrasion resistant and/or ballistic applications. With complete control of the manufacturing process from Steel making to heat treatment Algoma is able to maintain complete quality control over all its products.

4 Algoma s heat Treat facility is registered to TS s heat - Treated Plate is rapidly quenched by 40,000 gallons of water per minute, sprayed under high pressure on both top and bottom surfaces simultaneously, over the full surface of the Plate . This unique quench system is part of a process that enables Algoma to deliver heat - Treated Plate with user-friendly characteristics and longer life in abrasive applications. Rapid cooling ensures through-thickness hardness, and the virtually scale-free surface allows easy flame-cutting and welding without surface preparation.

5 Essar Steel Algoma offers fast, direct shipping to all of North America by rail, road or water, plus full technical support from a team of technical service representatives, development engineers, and product InformationWeldingAlgoma s heat -treat facility produces a low alloy Plate that is easy to weld using simple procedures and common, readily available carbon contents and carbon equivalents of Algoma heat - Treated plates are similar to those of many medium- and high-strength alloy carbon steels. A high resistance to hydrogen-induced cold cracking is inherent when proper welding procedures are employed as outlined in the next sound welds depend on good joint preparation, the temperature of the material, joint restraint and the use of the appropriate low-hydrogen consumables.

6 Please consult your welding consumable supplier for the appropriate heat input processes such as electrogas and electroslag should not be used, as they can adversely affect Plate properties in and adjacent to the heat affected a weld will be exposed to abrasives, most of the joint can be filled with lower-strength material, with a capping layer of abrasion- resistant weld metal applied to complete the heat - Treated steels are sensitive to heat : in welding, stress relief and elevated temperature service. Holding the Steel at or near stress relieving temperatures for any length of time will result in lower mechanical properties.

7 The length of time at temperature will determine the potential flame cut heat - Treated Plate that is going to be subjected to dynamic loading, forming, or restraint during welding, it is recommended that the Plate edges be ground or machined to remove the hardened layer that results from the cutting cuttingAll grades of Algoma heat - Treated Plate are easy to cut using the proper shop and field recommends the smallest possible torch tip combined with the fastest possible cutting speed to flame cut Algoma heat - Treated Plate , since all heat - Treated Plate products are sensitive to heat .

8 A small tip will minimize the heat effect and ensure minimal degradation of the Steel s inherent s virtually scale-free surface will improve the smoothness of the oxyfuel cut and will generally eliminate blowback. For multiple cuts, balanced torch settings will minimize ResultsHow to get the best results with Essar Steel Algoma s heat Treated Mn6Cu + Ni15Cr + Mo + V5C+=++The carbon equivalent on the data sheets for each grade is calculated using the Deardon O Neil formula:Hardness 60 0 40 0 30 0 20 0 60 0 50 0 40 0 30 0 20 0 2 46 8 10 12 14 16 mm 50 0 HBHv AlgoTAlgoTAlgoTuf 500uf 450F uf 400F Algoma 100/130 Distance from edge Measured at midthickness, 3/8 ( mm) min.

9 Thickness0 1/8 in 0 1/4 3/8 1/ 2 5/ 8 The attached figure shows the softening effect of oxy acetylene cutting along the flame cut cutting is ideal for Algoma heat - Treated Plate : the cut will be smoother than with the oxyfuel process and the depth of the heat -affected zone will be avoid cracking, Algoma heat - Treated Plate should be at least room temperature for flame cutting. For AlgoTuf 400F plates (38mm) and thicker, AlgoTuf 450F plates (16mm) and thicker and all thicknesses of AlgoTuf 500, a preheat temperature of 210 F (100 C) is and punching Both Algoma 100 and 130 grades, up to (12mm), can be either sheared or punched using equipment of sufficient capacity.

10 The punch diameter should be at least times the Plate thickness. Tools must be kept in good working order and operator safety measures must be followed. Algoma does not recommend that the AlgoTuf grades be either sheared or punched because of their high strength and hardness levels. Excessive tool wear, broken punches and/or damage to the shear or punch equipment could (see the machining chart)Algoma heat - Treated Plate is easy to machine, using the proper cutting tools, speeds and feed rates. Cutting speeds greater than Algoma s recommendations can cause rapid tool deterioration.