LEXAN™ Resin HP4 Americas: COMMERCIAL

1 LEXAN Resin HP4. Americas: COMMERCIAL . Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP. Class VI). EtO and steam sterilizable. Contains mold release. TYPICAL PROPERTIES TYPICAL value unit Standard MECHANICAL. psi ASTM D 638. Tensile Stress, yld, Type I, in/min 8900. Tensile Stress, brk, Type I, in/min 9800 psi ASTM D 638. Tensile Strain, yld, Type I, in/min 7 % ASTM D 638. Tensile Strain, brk, Type I, in/min 130 % ASTM D 638. Tensile Modulus, in/min 343000 psi ASTM D 638. Flexural Stress, yld, in/min, 2 in span 14000 psi ASTM D 790.

2 Flexural Modulus, in/min, 2 in span 339000 psi ASTM D 790. Hardness, Rockwell M 70 - ASTM D 785. Hardness, Rockwell R 118 - ASTM D 785. Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044. Tensile Stress, yield, 50 mm/min 63 MPa ISO 527. Tensile Stress, break, 50 mm/min 70 MPa ISO 527. Tensile Strain, yield, 50 mm/min 6 % ISO 527. Tensile Strain, break, 50 mm/min 110 % ISO 527. Tensile Modulus, 1 mm/min 2350 MPa ISO 527. Flexural Stress, yield, 2 mm/min 90 MPa ISO 178. Flexural Modulus, 2 mm/min 2300 MPa ISO 178. IMPACT. ft-lb/in ASTM D 4812. Izod Impact, unnotched, 73 F 60. Izod Impact, notched, 73 F 15 ft-lb/in ASTM D 256.

3 Izod Impact, notched (natural, tints) 15 ft-lb/in ASTM D 256. Izod Impact, notched (colors) 15 ft-lb/in ASTM D 256. (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are (2) Only typical data for selection purposes. Not to be used for part or tool design. measured after at least 48 hours storage at 23 C/50% relative humidity. All properties, except the melt volume (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are conditions.

4 Prepared according to ISO 294. (4) Internal measurements according to UL standards. (5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. (6) Needs hard coat to consistently pass 60 sec Vertical Burn. Source GMD, last updated: PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA. DISCLAIMER : THE MATERIALS, PRODUCTS AND SERVICES OF SAUDI BASIC INDUSTRIES CORPORATION (SABIC) OR ITS SUBSIDIARIES OR AFFILIATES (SELLER) ARE SOLD SUBJECT TO SELLERS STANDARD.

5 CONDITIONS OF SALE, WHICH ARE AVAILABLE UPON REQUEST. INFORMATION AND RECOMMENDATIONS CONTAINED IN THIS DOCUMENT ARE GIVEN IN GOOD FAITH. HOWEVER, SELLER MAKES NO. EXPRESS OR IMPLIED REPRESENTATION, WARRANTY OR GUARANTEE (i) THAT ANY RESULTS DESCRIBED IN THIS DOCUMENT WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE. EFFECTIVENESS OR SAFETY OF ANY DESIGN OR APPLICATION INCORPORATING SELLERS MATERIALS, PRODUCTS, SERVICES OR RECOMMENDATIONS. UNLESS OTHERWISE PROVIDED IN SELLERS. STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS, PRODUCTS, SERVICES OR RECOMMENDATIONS DESCRIBED IN THIS.

6 DOCUMENT. Each user is responsible for making its own determination as to the suitability of Sellers materials, products, services or recommendations for the users particular use through appropriate end-use and other testing and analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Sellers Standard Conditions of Sale or this Disclaimer, unless it is specifically agreed to in a writing signed by Seller. Statements by Seller concerning a possible use of any material, product, service or design do not, are not intended to, and should not be construed to grant any license under any patent or other intellectual property right of Seller or as a recommendation for the use of any material, product, service or design in a manner that infringes any patent or other intellectual property right.

7 SABIC and brands marked with are trademarks of SABIC or its subsidiaries or affiliates. 2017 Saudi Basic Industries Corporation (SABIC). LEXAN Resin HP4. Americas: COMMERCIAL . TYPICAL PROPERTIES TYPICAL value unit Standard IMPACT. ft-lb/in ASTM D 1822. Tensile Impact, Type S 274. Falling Dart Impact (D 3029), 73 F 124 ft-lb ASTM D 3029. Instrumented Impact Energy @ peak, 73 F 557 in-lb ASTM D 3763. Izod Impact, unnotched 80*10*4 +23 C NA kJ/m ISO 180/1U. Izod Impact, unnotched 80*10*4 -30 C NA kJ/m ISO 180/1U. Izod Impact, notched 80*10*4 +23 C 12 kJ/m ISO 180/1A. Izod Impact, notched 80*10*4 -30 C 10 kJ/m ISO 180/1A.

8 Charpy Impact, notched, 23 C 35 kJ/m ISO 179/2C. Charpy 23 C, Unnotch Edgew 80*10*4 sp=62mm NA kJ/m ISO 179/1eU. Charpy -30 C, Unnotch Edgew 80*10*4 sp=62mm NA kJ/m ISO 179/1eU. THERMAL. F ASTM D 1525. Vicat Softening Temp, Rate B/50 309. HDT, 66 psi, in, unannealed 278 F ASTM D 648. HDT, 264 psi, in, unannealed 269 F ASTM D 648. CTE, flow, -40 F to 200 F 1/ F ASTM E 831. Specific Heat BTU/lb- F ASTM C 351. Thermal Conductivity W/m- C ASTM C 177. Thermal Conductivity W/m- C ISO 8302. CTE, 23 C to 80 C, flow 1/ C ISO 11359-2. Ball Pressure Test, 125 C +/- 2 C PASSES - IEC 60695-10-2. Vicat Softening Temp, Rate A/50 153 C ISO 306.

9 Vicat Softening Temp, Rate B/50 141 C ISO 306. Vicat Softening Temp, Rate B/120 142 C ISO 306. HDT/Be, Edgew 120*10*4 sp=100mm 136 C ISO 75/Be (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are (2) Only typical data for selection purposes. Not to be used for part or tool design. measured after at least 48 hours storage at 23 C/50% relative humidity. All properties, except the melt volume (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are conditions.

10 Prepared according to ISO 294. (4) Internal measurements according to UL standards. (5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. (6) Needs hard coat to consistently pass 60 sec Vertical Burn. Source GMD, last updated: PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA. DISCLAIMER : THE MATERIALS, PRODUCTS AND SERVICES OF SAUDI BASIC INDUSTRIES CORPORATION (SABIC) OR ITS SUBSIDIARIES OR AFFILIATES (SELLER) ARE SOLD SUBJECT TO SELLERS STANDARD.