LOCTITE 567™ - tdsna.henkel.com

Technical Data Sheet LOCTITE 567 . (TDS for the new formulation of LOCTITE 567 ) October-2017. PRODUCT DESCRIPTION ULC Classification LOCTITE 567 provides the following product Classified by Underwriters Laboratories of Canada Inc. characteristics: MH27131 - An anaerobic material which contains a lubricant Technology Acrylic and sets to form a tight seal and maintain a controlled locking Chemical Type Methacrylate ester strength. For use in joining threaded pipe connections or other Appearance (uncured) Smooth, creamy, off-white pasteLMS closely fitting metal parts in devices handling natural gas and Components One component - methane, gasoline and petroleum oils, and propane and requires no mixing butane at pressures not exceeding 13,790 kPa.

TDS LOCTITE® 567™, October-2017 % of Full Strength on Steel Cure Time 100 75 50 25 0 0min 30min 1h 3h 6h 24h 72h 168h Zinc phosphate Stainless steel Zinc dichromate Black oxide

Tags:

  Zinc

Information

Domain:

Source:

Link to this page:

Please notify us if you found a problem with this document:

Other abuse

Transcription of LOCTITE 567™ - tdsna.henkel.com

1 Technical Data Sheet LOCTITE 567 . (TDS for the new formulation of LOCTITE 567 ) October-2017. PRODUCT DESCRIPTION ULC Classification LOCTITE 567 provides the following product Classified by Underwriters Laboratories of Canada Inc. characteristics: MH27131 - An anaerobic material which contains a lubricant Technology Acrylic and sets to form a tight seal and maintain a controlled locking Chemical Type Methacrylate ester strength. For use in joining threaded pipe connections or other Appearance (uncured) Smooth, creamy, off-white pasteLMS closely fitting metal parts in devices handling natural gas and Components One component - methane, gasoline and petroleum oils, and propane and requires no mixing butane at pressures not exceeding 13,790 kPa.

2 Ignition Viscosity High temperature greater than 460 C. Classed less than 10 below Cure Anaerobic paraffin oil with respect to fire hazard. Note: This is a regional Secondary Cure Activator approval. Please contact your local Technical Service Center Application Thread sealing for more information and clarification. Strength Low NSF International Certified to ANSI/NSF Standard 61 for use in commercial and This Technical Data Sheet is valid for LOCTITE 567 residential potable water systems not exceeding 82 C. Note: manufactured from the dates outlined in the This is a regional approval.

3 Please contact your local Technical "Manufacturing Date Reference" section. Service Center for more information and clarification. LOCTITE 567 is designed for the locking and sealing of Approved by the Australian Gas Association Certificate metal tapered threads and fittings. The product cures when number 3207 Class III rated working pressure 2000 kPa, confined in the absence of air between close fitting metal working temperature -10 to 205 C. Note: This is a regional approval. Please contact your local Technical Service Center surfaces and prevents loosening and leakage from shock and for more information and clarification.

4 Vibration. LOCTITE 567 provides robust curing performance. It not only works on active metals ( brass, copper) but also on passive substrates such as stainless steel TYPICAL PROPERTIES OF UNCURED MATERIAL. and plated surfaces. The high lubricating properties of this Specific Gravity @ 25 C compound prevent galling on stainless steel, aluminum and all Flash Point - See SDS. other metal pipe threads and fittings. The product offers high Viscosity, Brookfield - RVF, 25 C, mPa s (cP): temperature performance and oil tolerance.

5 It tolerates minor Spindle 7, speed 2 rpm 280,000 to 800,000 LMS. surface contaminations from various oils, such as cutting, lubrication, anti-corrosion and protection fluids. LOCTITE . 567 is recommended for industrial applications in the TYPICAL CURING PERFORMANCE. chemical processing, petroleum refining, pulp/paper, waste treatment, textile, utilities/power generation, marine, Cure Speed vs. Substrate automotive, industrial equipment, gas compression and The rate of cure will depend on the substrate used. The graph distribution industries.

6 It is also recommended for industrial below shows the breakaway strength developed with time on M10 black oxide bolts and steel nuts compared to different plant fluid power systems. materials and tested according to ISO 10964. UL Classification Classified by Underwriters Laboratories Inc. MH8007 - Fire hazard is small. No flash point in liquid state. Ignition temperature 455 C. For use in devices handling gasoline, petroleum oils, natural gas (pressure not over 300. PSIG), butane and propane not exceeding 2 in. pipe size. Note: This is a regional approval.

7 Please contact your local Technical Service Center for more information and clarification. TDS LOCTITE 567 , October-2017. % of Full Strength on Steel 100 After 4 hours @ 22 C. Black oxide Breakaway Torque, ISO 10964: 3/8 x 24 steel nuts (grade N m 75 ha te 2) and bolts (grade 2) ( ) ( ). phosp zinc After 24 hours @ 22 C. 50 eel Removal Torque, ASTM D 6396, Pre-torqued to 27 N m: ss st inle 3/8 NPT steel pipe tees N m 50. Sta and plugs ( ) (445). 25. Breakaway Torque, ISO 10964, Unseated: zinc dichromate M10 black oxide bolts and steel N m 12.

8 Nuts ( ) (110). 0. 0min 30min 1h 3h 6h 24h 72h 168h M10 brass nuts and bolts N m 12. Cure Time ( ) (105). M10 zinc dichromate N m nuts and bolts ( ) (22). Cure Speed vs. Temperature M10 zinc N m The rate of cure will depend on the temperature. The graph phosphate nuts and bolts ( ) (82). below shows the breakloose strength developed with time at M10 stainless steel N m different temperatures on NPT 3/8 malleable steel tees and nuts and bolts ( ) (70). steel plugs, pretorqued to 27 N m and tested according to M6 black oxide bolts and N m ASTM D6396.

9 Steel nuts ( ) (8). M16 black oxide steel N m 13. nuts and bolts ( ) (115). 125. % of Full Strength on Steel 3/8 x 24 steel nuts (grade N m 40 C 2) and bolts (grade 2) ( ) ( 15). 100. Prevail Torque, ISO 10964, Unseated: 22 C M10 black oxide bolts and steel N m 75. nuts ( ) (17). 5 C M10 brass nuts and bolts N m 50 ( ) (19). M10 zinc dichromate N m 25 nuts and bolts ( ) (12). M10 zinc N m phosphate nuts and bolts ( ) (11). 0 M10 stainless steel N m 0min 30min 1h 3h 6h 24h 72h 168h nuts and bolts ( ) (12). Cure Time M6 black oxide bolts and N m steel nuts ( ) ( ).

10 Cure Speed vs. Activator M16 black oxide steel N m Where cure speed is unacceptably long, or large gaps are nuts and bolts ( ) (20). present, applying activator to the surface will improve cure speed. The graph below shows the breakloose strength developed with time using Activator SF 7471 , SF 7649 Breakloose Torque, ISO 10964, Pre-torqued to 5 N m: and SF 7091 on M10 stainless steel nuts and bolts and M10 black oxide bolts and steel N m 17. nuts ( ) (150). tested according to ISO 10964. Prevail Torque, ISO 10964, Pre-torqued to 5 N m: 100 M10 black oxide bolts and steel N m % of Full Strength on Steel Activator SF 7091 nuts ( ) (20).