Transcription of Rigid 10K - Formlabs
1 Rigid RESINR igid 10 KResin for Rigid , Strong, Industrial-Grade PrototypesThis highly glass-filled resin is the stiffest material in our engineering portfolio. Choose Rigid 10K Resin for precise industrial parts that need to withstand significant load without bending. Rigid 10K Resin has a smooth matte finish and is highly resistant to heat and injection molds and insertsHeat resistant and fluid exposed components, jigs, and fixturesSimulates stiffness of glass and fiber-filled thermoplasticsAerodynamic test modelsPrepared10 . 07 . 2020To the best of our knowledge the information contained herein is accurate. However, Formlabs , Inc. makes no warranty, expressed or implied, regarding the accuracy of these results to be obtained from the use.
2 07 . 2020V1 FLRG1001* May not be available in all regionsMATERIAL PROPERTIES DATAR igid 10K ResinMETRICIMPERIAL 1 METHODG reenUV Post-cured 1UV + Thermal 2 Green 2UV Post-cured 1UV + Thermal 2 Tensile PropertiesUltimate Tensile Strength55 MPa 65 MPa 53 MPa 7980 psi 9460 psi 7710 psiASTM D638-14 Tensile GPa10 GPa10 GPa1090 ksi1480 ksi1460 ksiASTM D638-14 Elongation at Break2%1%1%2%1%1%ASTM D638-14 Flexural PropertiesFlexural Strength84 MPa126 MPa103 MPa12200 psi18200 psi15000 psiASTM D 790-15 Flexural Modulus6 GPa9 GPa10 GPa905 ksi1360 ksi1500 ksiASTM D 790-15 Impact PropertiesNotched IZOD16 J/m16 J/m18 ft- ft- ft-lbf/inASTM D256-10 Unnotched IZOD41 J/m47 J/m41
3 Ft- ft- ft-lbf/inASTM D4812-11 Thermal PropertiesHeat Deflection Temp. @ MPa56 C 82 C 110 C 133 F 180 F 230 FASTM D 648-16 Heat Deflection Temp. @ MPa65 C163 C218 C149 F325 F424 FASTM D 648-16 Thermal Expansion, 0-150 C48 m/m/ C47 m/m/ C46 m/m/ C27 in/in/ F26 in/in/ F26 in/in/ FASTM E 831-13 SOLVENT COMPATIBILITYP ercent weight gain over 24 hours for a printed and post-cured 1 x 1 x 1 cm cube immersed in respective solvent:Solvent24 hr weight gain, %Solvent24 hr weight gain, %Acetic Acid 5%< (aka gasoline)0 Acetone< oil (light) Alcohol< oil (Heavy)< ~5% Water ( NaCl) Hydroxide solution ( PH 10) < glycol Monomethyl < Acid (HCl conc) glycol monomethyl peroxide (3%)< Gas GenerationTesting Standard BSS 7239 (comparable to NFPA No.)
4 258)Maximum allowed concentration per BSS 7239 (ppm)Flaming Mode (ppm)Non-Flaming Mode (ppm)Hydrogen Cyanide (HCN) Monoxide (CO)35005010 Nitrous Oxides (NOx)100< 2< 2 Sulfur Dioxide (SO2)100< 1< 1 Hydrogen Fluoride (HF)200< < Chloride (HCl)5001< 1 FlammabilityTesting StandardRatingUL 94 Section 7 (3 mm)HBSmoke DensitySpecific Optical DensityTesting Standard@ 90 sec@ 4 minMaximumASTM E662 Flaming Mode295132 ASTM E662 Non-Flaming Mode0163 All testing specimens were printed using Form 31 data was obtained from parts printed using Form 3, 100 m and post-cured with a Form Cure for 60 minutes at 70 data was obtained from parts printed using Form 3, 100 m and post-cured with a Form Cure for 60 minutes at 70 C and an additional thermal cure at 90 C for 125 minutes.