Rivolta S.K.D. 5001/5002 - chlc.com.hk

1 Rivolta 5001/5002 high performance greases for highest temperature Rivolta 5001/5002 are special fully synthetic greases based on a fluorine oil and a special thickener. This combination gives a thermal stability to the products superior to conventional high temperature greases. With this products lubricate even up to the temperature limit for lubricants (250 C) and it offers full lubrication even when aggressive mediums are are qualified for the lubrication of roller and plain bearings as well as of other sliding Lubrication of roller and plain bearings at high temperatures: -Bearings in electromotors, fans and compressors; -Roller bearings in calenders or coating machines; -Guide rollers of transport chains of textile machines; -Impellers in ovens or autoclave carts.

2 -Guiding and deflection rollers at conveyors, baking automats and drying stoves Bearings and guides when aggressive mediums are present in the chemical industry, galvanic industry and metal-working industry Lubrication of plastics and sealing materials A BAM-approval for 5002 for the lubrication in the oxygen area Product Strength Outstanding operative temperature range from -20 C up to +260 C, can reach a high operative temperature for a very long duration. Frequent lubrications can be omitted Offer stable penetration and aging resistance and thus minimize maintenance cost and labor costs due to extended service intervals Excellent protection against corrosion, even at extreme conditions.

3 It provides long lubricant service life and can resist against water, steam, solvents, lyes and acids Low evaporation loss and low consumption of lubricant to guarantee a long period of service life Registered by NSF as a H1-lubricant, the products fulfill the strict demands of food hygiene and quality assurance system. Any small leakage would not cause the stop of production lineProcessingRivolta 5001 / 5002 are not mixable with products based on mineral using Rivolta 5002, clean lubrication point thoroughly. The high technical qualities of our product are only obtainable when using it on clean metal 5001/5002 Made in GermanyTechnical dataUnit of 5002 Densityg/mlDIN of base oil at 40 Cmm /sDIN 51562/1510500 NLGI-grade-DIN 5181812 Worked penetration1/10 mmDIN ISO 2137310-340265-295 PW 100,000 Decrease of worked penetration after 100,000 double cycles1/10 mm-< 20< 20 Operative temperature range C--25 to +260-20 to +260 Dropping point CDIN ISO 2176nonenoneCorrosion protection to steel (SKF-Emcor)

4 518020 / 00/0 Corrosion effect on 518111 at 200 C1 at 200 COil separation at 200 C%DIN 51817< 5< 3 Behavior against water 5d/RT-DIN 51807 Test*Friction coefficient Wear rate ball disc-mm mDIN * Swing friction wear tester, T = 125 C, loading rises from F = 50 N up to F = 200 N during 2 hours Packing in 800 cartridge, 1kg tin and 10 kg pailNSF-H1