RUTILE & BASIC - Fsh Welding

1 RUTILE & BASIC ARC Welding ELECTRODES RUTILE ELECTRODES 48 SP (E 6013) 51 (E 6013) 54 (E 6013) D6 (E 6013) 160 (E 7024) Universal all position RUTILE electrode . Easy striking. Easy to weld with. Recommended for poor quality steels. All position RUTILE electrode . Especially designed for Welding piping systems. Current applications. Locksmithing, metal construction. Heavily coated RUTILE electrode with an excellent weld bead appearance. All positions except vertical down. General Welding of mild steel constructions.

2 RUTILE electrode especially designed for vertical down Welding . Locksmithing and maintenance Welding . High efficiency (160 %) RUTILE electrode . Excellent weld bead appearance. Very high deposit speeds. CELLULOSE ELECTRODES 6010 (E 6010) electrode with cellulose coating. Deep penetration Welding . All positions. Piping systems. Welding and repairing. BASIC ELECTRODES B 56 (E 7018-1) B 7016 SP (E 7016) Universal BASIC electrode . Welding of restrained parts or parts subjected to stress. Heavy structures. Shipbuilding. Pressure vessels. BASIC electrode with double coating. Welding and repairing.

3 Exceptional Welding characteristics. Stable arc. Few spatters. Recommended for root passes and on badly prepared joints. BASIC ELECTRODES FOR CREEP RESISTANT STEELS B60 (E 7018-A1) B 61 (E 8018-B1) B 63 (E 8018-B2) B 68 (E 9018-B3) B 69 (E 502-15) Low hydrogen BASIC electrode with Mo for Welding steels resistant to temperatures up to 500 C. Piping systems, boilers. Low hydrogen BASIC electrode with Cr and Mo for Welding creep resistant steels up to 500 C. Cr, Mo, Chromesco 1 Piping systems, boilers. Chemical and petrochemical industries. Low hydrogen BASIC electrode with Cr and Mo for Welding creep resistant steels up to 550 C. 1% Cr, Mo Chemical and petrochemical industries.

4 Low hydrogen BASIC electrode with Cr and Mo for Welding creep resistant steels up to 600 C. 2% Cr, 1% Mo, Chromesco 3 Good resistance in the presence of hydrogen. Overheaters, valve bodies, Boilers, hydrocrackers. Low hydrogen BASIC electrode with Cr and Mo for Welding creep resistant steels up to 600 C. 5% Cr, Mo Highly resistant to hot gases and overheated steam. Heat exchangers, Steam boilers, overheaters. BASIC ELECTRODES FOR HIGH YIELD STRENGTH STEELS B 70 (E 10018-G) B 72 (E 9018-G) B 73 (E 9018-D1) High strength BASIC coated electrode highly resistant to cracking. High security Welding . Low hydrogen BASIC coated electrode with high yield strength. For Welding 550<RM<770 MPa steels.

5 Rail of travelling crane, sliding guide surfaces. Low hydrogen BASIC coated electrode with high yield strength for Welding fine grain steels applied at temperatures between 50 and +500 C. Good resistance to fatigue and corrosion in the presence of phosphorus and sulphur. a BASIC ELECTRODES FOR HIGH YIELD STRENGTH STEELS B 75 CU (E 8018-W) B 77 (E 11018-M) Low hydrogen BASIC coated electrode with a deposit consisting of copper, chromium and molybdenum for Welding all steels resistant to atmospheric corrosion (industrial sea). Welding "Cor-Ten" steels. Public equipment. Tanks, sidings, bridges, roofing, etc. BASIC electrode with a high strength steel deposit very resistant to cracking at service temperatures between 40 C and +450 C.

6 Very low diffusible hydrogen (<3ml H2/100g metal deposit) Pressure vessels BASIC ELECTRODES FOR COLD TOUGH STEELS B 81 (E 8018-C3) B 82 (E 8018-C1) B 84 (E 8018-C2) Low hydrogen BASIC coated electrode with 1% nickel. Toughness resistant to temperatures down to 60 C. Mechanical lifting equipment, structures, etc. Low hydrogen BASIC coated electrode with % nickel for Welding fine grain steels resistant to low temperatures. Tanks, liquid gas distribution pipes, Offshore, petrochemical industry. Low hydrogen BASIC coated electrode with about 3 % nickel for Welding fine grain steels resistant to very low temperatures between -60 C and 80 C.

7 Cyrogenic and petrochemical industries. Place des Forges 90600 Grandvillars France T l. + 33 (0)3 84 57 37 77 Fax + 33 (0)3 84 23 57 90 GB 236-07 Ru/Ba