SC-10 - Core Metal

1 AWS E6010 JIS Z3211 D4310EN EN499 E 38 0 C 2 5 DESCRIPTION : SC-10 is a high cellulose all-position electrode designed for deep penetration on root and filler layers of butt or fillet welding. It has stable arc, fast frozen weld, easy control of :It is used for welding mild steel in pipeline, storage tank, pressure vessels and heavy contruction works. NOTE ON USAGE :1. Rebake the electrodes at 70-80 C for 30-60 minutes prior to use. 2. Clean up the the base Metal to be free from contamination. Weld Metal Analysis :Carbon (C) (Mn) (Si) (P) (S) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 425TS N/mm2 495EL%28 TYPICAL IMPACT VALUES :IV 0 C J83IV -30 C J70 APPROVALS AND CONFORMANCES :SIZES AND RECOMMENDED CURRENT RANGE (DC <+>)DiameterLengthmmmmFV & - 8040 - - 13060 - - 18090 - - 200120 - 180SC-10 MILD STEEL ELECTRODESAmpTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :-- 1-1 -SOREXAWS E6011 JIS Z3211 D4311EN EN499 E 38 0 C 1 5 DESCRIPTION :SC-11 is a high cellulose all-position electrode designed for deep penetration on root and filler layers of butt or fillet welding using either AC or DC+ current.

2 It has stable arc, goodporosity resistance and slag removability and good X-ray :It is suitable for welding mild steel in shipbuilding, pipeline, storage tank, pressure ON USAGE :1. Rebake the electrodes at 70-80 C for 30-60 minutes prior to use. 2. Clean up the the base Metal to be free from contamination. Weld Metal Analysis :Carbon (C) (Mn) (Si) (P) (S) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 428TS N/mm2 498EL%27 TYPICAL IMPACT VALUES :IV 0 C J80IV -30 C J50 APPROVALS AND CONFORMANCES :SIZES AND RECOMMENDED CURRENT RANGE (AC or DC <+>)DiameterLengthmmmmFV & - 9050 - - 12075 - - 17090 - - 200120 - 180SC-11 MILD STEEL ELECTRODESTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :-Amp- 1-2 -SOREXAWS E6013 JIS Z3211 D4313EN EN499 E 38 0 R 1 2 DESCRIPTION :SM-13 is a high titania electrode designed for all position welding including vertical downposition with good weldability and nice bead :It is used for welding of steel structures of shipbuilding, railway vehicles and cars.

3 It is also suitable for thin pipe and other ornamental works. NOTE ON USAGE :1. Dry the electrodes at 80-100 C for 30-60 minutes prior to use. 2. Clean up the the base Metal to be free from contamination. Weld Metal Analysis :Carbon (C) (Mn) (Si) (P) (S) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 422TS N/mm2 468EL%26 TYPICAL IMPACT VALUES :IV 0 C AND CONFORMANCES :SIZES AND RECOMMENDED CURRENT RANGE (DC <+>)DiameterLengthmmmmFV & - 9050 - - 12080 - - 160100 - - 220140 - 200 AmpMILD STEEL ELECTRODESTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :-SM-13- 1-3 -SOREXAWS E7016 JIS Z3212 D5016EN EN499 E 42 2 B 1 2 DESCRIPTION :SL-50 is a low hydrogen type electrode for the welding of high tensile steel. The weldingcan be done with stable arc, less spatter, good slag removability, good slag coveringand good X-ray soundness.

4 APPLICATIONS :It is suitable for low alloy steels, medium carbon steels, heavy steel plates, cast steels and steels of poor weldability. NOTE ON USAGE :1. Rebake the electrodes at 300-350 C for 60 minutes and keep at 100-150 C before use. 2. Take the backstep method to prevent blowholes at the arc starting. 3. Keep the arc as short as possible. Weld Metal Analysis :Carbon (C) (Mn) (Si) (P) (S) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 496TS N/mm2 564EL%30%TYPICAL IMPACT VALUES :IV -30 C J131 APPROVALS AND CONFORMANCES :-SIZES AND RECOMMENDED CURRENT RANGE (AC or DC <+>)DiameterLengthmmmmFV & - 8550 - - 13090 - - 180130 - - 240160 - 200-AmpSL-50 MILD STEEL AND HIGH TENSILE STEEL ELECTRODESTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :- 1-4 -SOREXAWS E7028 JIS Z3212 D5026EN EN499 E 42 2 B 7 4 DESCRIPTION :SL-56 is an iron powder and 490N/mm2 high tensile steel electrode .

5 It has a good crackresistance, good mechanical properties and easy slag removal. APPLICATIONS :It is suitable for welding in shipbuilding, bridges, and vehicles with high recovery rate. NOTE ON USAGE :1. Dry the electrodes at 300-350 C for 60 minutes and keep at 100-150 C before use. Weld Metal Analysis :Carbon (C) (Mn) (Si) (P) (S) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 550TS N/mm2 552EL% IMPACT VALUES :IV -20 C AND CONFORMANCES :-SIZES AND RECOMMENDED CURRENT RANGE (AC or DC <+>)DiameterLengthmmmmFV & - 8550 - - 13090 - - 180130 - - 240160 - 200SL-56-AmpMILD STEEL AND HIGH TENSILE STEEL ELECTRODESTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :- 1-5 -SOREXAWS E7018 JIS Z3212 D5016EN EN499 E 42 3 B 3 2 DESCRIPTION :SL-58 is a low hydrogen type electrode for the welding of 50kgf/mm2 grade high tensilesteel. The welding can be done with high deposition rate, good X-ray soundness andmechanical properties.

6 APPLICATIONS :It is especially suitable for nuclear power stations, petroleum chemical plants, and heavysteel plates. NOTE ON USAGE :1. Rebake the electrodes at 300-350 C for 60 minutes and keep at 100-150 C before use. 2. Keep the arc as short as possible. Weld Metal Analysis :Carbon (C) (Mn) (Si) (P) (S) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 518TS N/mm2 604EL%28%TYPICAL IMPACT VALUES :IV -29 C J156IV -46 C J128 APPROVALS AND CONFORMANCES :SIZES AND RECOMMENDED CURRENT RANGE (AC or DC <+>)DiameterLengthmmmmFV & - 8550 - - 13085 - - 180110 - - 230150 - - 240150 - 180 TYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :-AmpSL-58 MILD STEEL AND HIGH TENSILE STEEL ELECTRODES- 1-6 -SOREXAWS E10018 MJIS Z3212 D7016EN EN757 62 4 B 4 2 DESCRIPTION :SL-108M is a low hydrogen electrode designed for welding 690N/mm2 grade high tensile can obtain good heat resistance and grate crack resistance because of its low hydrogen composition in the weld Metal .

7 APPLICATIONS :In addition to the welding before hardfacing, it is suitable for the welding of 640-735N/mm2grade high tensile steel. NOTE ON USAGE :1. Rebake the electrodes at 300-350 C for 60 minutes and keep at 100-150 C before use. 2. Keep the arc as short as possible. 3. Backstep is the welding method to prevent blowholes during the arc starting4. Preheating the plates at 100 C before weldingWeld Metal Analysis :Carbon (C) (Mn) (Si) (Cr) (Ni) (Mo) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 638TS N/mm2 725EL%22 TYPICAL IMPACT VALUES :IV 50 C J60 APPROVALS AND CONFORMANCES :SIZES AND RECOMMENDED CURRENT RANGE (DC <+>) - 200180 - 250 MILD STEEL AND HIGH TENSILE STEEL ELECTRODESTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :240 - 300-AmpF100 - 140- 1-7 -SOREXAWS E11018 MJIS Z3212 D8016EN EN757 62 4 B 4 2 DESCRIPTION :SL-118M is an iron power low hydrogen electrode designed for welding 780N/mm2 gradehigh tensile steel.

8 It can obtain good heat resistance and excellent mechanical properties. APPLICATIONS :It is suitable for the welding of WEL TEN-80 high tensile steel as well. NOTE ON USAGE :1. Rebake the electrodes at 300-350 C for 60 minutes and keep at 100-150 C before use. 2. Keep the arc as short as possible. 3. Backstep is the welding method to prevent blowholes during the arc starting4. Preheating the plates at 100 C before weldingWeld Metal Analysis :Carbon (C) (Mn) (Si) (Cr) (Ni) (Mo) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 695TS N/mm2 785EL%23 TYPICAL IMPACT VALUES :IV 50 C AND CONFORMANCES :-SIZES AND RECOMMENDED CURRENT RANGE (DC <+>) STEEL AND HIGH TENSILE STEEL ELECTRODESTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :-AmpF100 - 140140 - 200180 - 250240 - 300- 1-8 -SOREXAWS E11016-GJIS Z3212 D8016EN EN757 62 2 Mn2 NiMo B 1 2 DESCRIPTION :SL-110 is a low hydrogen electrode designed for welding 690N/mm2 grade high tensile can obtain good heat resistance and excellent mechanical properties in all position because of its low hydrogen composition.

9 APPLICATIONS :It is also used for build-up welding before ON USAGE :1. Rebake the electrodes at 300-350 C for 60 minutes and keep at 100-150 C before use. 2. Keep the arc as short as possible. 3. Backstep is the welding method to prevent blowholes during the arc starting4. Preheating the plates at 100 C before weldingWeld Metal Analysis :Carbon (C) (Mn) (Si) (Cr) (Ni) (Mo) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 682TS N/mm2 760EL%23 TYPICAL IMPACT VALUES :IV 50 C AND CONFORMANCES :SIZES AND RECOMMENDED CURRENT RANGE (DC <+>) - 200180 - 250240 - 300 AmpFTYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :100 - 140SL-110 MILD STEEL AND HIGH TENSILE STEEL ELECTRODES-- 1-9 -SOREXAWS E7016-A1 JIS Z3223 DT1216EN EN1599 E Mo B 1 2 DESCRIPTION :SR-76A1 is a low hydrogen electrode alloyed with Mo for welding steels of pressurevessels.

10 APPLICATIONS :It is suitable for welding steel used at high temperature and high pressure ( ATPA12, A335-P1 of Steel Pipes, STBA 12, A209-T1, A161-T1 of heat exchanger, A217-WCI casting steel and A182-F1, A366-F1 of forging steels). NOTE ON USAGE :1. Rebake the electrodes at 300-350 C for 60 minutes and keep at 100-150 C before use. 2. Keep the arc as short as possible. Weld Metal Analysis :Carbon (C) (Mn) (Si) (Mo) (P) (S) MECHANICAL PROPERTIES OF WELD Metal :YP N/mm2 505TS N/mm2 582EL%31 Heat Treatment : 620 C X 1hrAPPROVALS AND CONFORMANCES :SIZES AND RECOMMENDED CURRENT RANGE (AC or DC <+>)DiameterLengthmmmmFV & ~13080~ ~180120~ ~230 LOW ALLOY STEEL ELECTRODES FOR HEAT RESISTANT STEEL TYPICAL CHEMICAL COMPOSITION OF WELD Metal (wt%) :-AmpSR-76A1- 1-10 -SOREXAWS E7018-A1 JIS Z3223 DT1216EN EN1599 E Mo B 3 2 DESCRIPTION :SR-78A1 is an iron powder low hydrogen electrode alloyed with Mo for welding chemicalindustries, oil refinery plants and turbine casting steels.