SCHEDA TECNICAGRUPPO LUCEFINREVISIONE 2012 DIRITTI RISERVATII VALORI RIPORTATI SONO INDICATIVI E POSSONO SUBIRE MODIFICHE E AGGIORNAMENTI IN QUALSIASI MOMENTO. Lucefin SI ESONERA DA EVENTUALI RESPONSABILIT E CONSEGUENZE DERIVANTI DAL LORO UTILIZZO.
scheda tecnica gruppo lucefin revisione 2012 diritti riservati i valori riportati sono indicativi e possono subire modifiche e aggiornamenti in qualsiasi momento.
Domain:
Source:
Link to this page:
1 SCHEDA TECNICAGRUPPO LUCEFINREVISIONE 2012 DIRITTI RISERVATII VALORI RIPORTATI SONO INDICATIVI E POSSONO SUBIRE MODIFICHE E AGGIORNAMENTI IN QUALSIASI MOMENTO. Lucefin SI ESONERA DA EVENTUALI RESPONSABILIT E CONSEGUENZE DERIVANTI DAL LORO UTILIZZO.
Qualità materiale X5CrNiCuNb16-4 Scheda Tecnica Numero 1.4 54 2 Acciaio Inossidabile Indurente per precipitazione Lucefin Group Composizione chimica C% …
Qualità materiale X5CrNi18-10 Scheda Dati Numero 1.4 301 Acciaio Inossidabile Austenitico Lucefin Group Composizione chimica …
X6CrNiMoTi17-12-2 n° 1.4571 austenitic stainless steel Lucefin Group Typical values at high temperature properties.For information only R …
51CrV4 1.8159 Lucefin Group Cold-drawn + quenched and tempered +C +QT EN 10277-5: 2008 Hot-rolled annealed + peeled-reeled +A +SH size Testing at …
Quality C45E Technical card According to standards EN 10083-2: 2006 Lucefin Group Number 1.1191 Chemical composition C% Si% max Mn% P% max S% max Cr% max Mo%
Quality SAE 1018 Technical card According to standards ASTM A 576-90b: 2000 Hot rolled Lucefin Group ASTM A 311/A 311M: 2004 …
X14CrMoS17 n° 1.4104 martensitic stainless steel Lucefin Group Effect of cold-working (hot-rolled +RA+C). Approximate values R N/mm 2 550 570 600 620 650 710 755 765 775
Quality X46Cr13 Technical card Number 1.4034 Martensitic Stainless Steel Lucefin Group Chemical composition C% Si% max Mn% max P% max S% a) max Cr% 0,43-0,50 1,00 1,00 0,040 0,015 12,5-14,5
Quality C45E According to standards EN 10083 2: 2006 Number 1.1191
Lucefin experience; Forged round 300 mm quenched at 870 °C in water, tempered 590 °C air Longitudinal Testing R Rp 0.2 A% C% Kv +20°C Kv -20°C HB Depth from Heat Treatment surface N/mm 2 N/mm 2 J J ½ radius 1201 1110 12,8 55,0 90-98-90 62-58-60 371 Chemical composition %
Caratteristiche meccaniche di prodotto in longitudinale Trattamento termico Ø 0.2 0 °C 18 °C 46 °C