Supercored 71H(Rev04) [호환 모드] - HYUNDAI …

1 Rev. 04. Supercored 71H. FLUX CORED ARC welding consumables . FOR welding OF Mild & 490 Mpa CLASS. HIGH TENSILE STEEL. HYUNDAI welding CO., LTD. Supercored 71H. v Specification AWS E71T1-C1A4-CS1. (AWS E491T1-C1A4-CS1). (AWS E71T-1C/ -9C/ -9C J). EN ISO 17632-A T 42 4 P C1 1H5. v Applications All position welding of shipbuilding, bridge, building and structural Fabrications. v Characteristics Supercored 71H is a titania flux cored wire for all position welding on Usage with high amperage. Its impact value is very good under high heat input, arc is smooth and slag detachability is excellent.

2 V Note on Usage 1. Proper preheating(50~150 , 122~302 ) and interpass temperature must be used in order to release hydrogen which may cause cracking in weld metal when electrodes are used for medium and heavy plates 2. One-side welding defect such as hot cracking may occur with welding parameter such as high welding speed. 3. Use 100% CO2 gas. Supercored 71H. Mechanical Properties & Chemical Composition of All Weld Metal v welding Conditions Method by AWS Rules welding Position : 1G(PA). Diameter : ( ). Shielding Gas : 100%CO . Flow Rate : 20 /min Volt.

3 : 280A / 32V. 20~25mm Stick-Out : ( ~ ). Pre-Heat : . Interpass Temp. : 150 15 (302 59 ). [ Joint Preparation & Layer Details ] Polarity : DC(+). v Mechanical Properties of the weld metal CVN Impact Test Consumable Tensile Test J(ft lbs). YS TS EL -30 -40 . Mpa (Ksi) Mpa (Ksi) (%) (-22 ) (-40 ). Supercored 71H. 550 (80) 570 (83) 90 (66) 60 (44). AWS 400 490~660 27J at 40 . 22. E71T1-C1A4-CS1 (58) (70~95) ( 20ft lbs at -40 ). v Chemical Analysis of the weld metal(wt%). Brand Name C Si Mn P S. Supercored 71H AWS E71T1-C1A4-CS1. This information is provided solely for the purpose of confirming product conformance with applicable standards.

4 The serviceability of a product or structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI . welding CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure, shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements. Supercored 71H. Mechanical Properties & Chemical Composition of All Weld Metal v welding Conditions Method by AWS Rules welding Position : 1G(PA).

5 Diameter : ( ). Shielding Gas : 100%CO . Flow Rate : 20 /min Volt. : 300A / 32V. 20~25mm Stick-Out : ( ~ ). Pre-Heat : . Interpass Temp. : 150 15 (302 59 ). [ Joint Preparation & Layer Details ] Polarity : DC(+). v Mechanical Properties of the weld metal CVN Impact Test Consumable Tensile Test J(ft lbs). YS TS EL -30 -40 . Mpa (Ksi) Mpa (Ksi) (%) (-22 ) (-40 ). Supercored 71H. 550 (80) 570 (83) 85 (63) 60 (44). AWS 400 490~660 27J at 40 . 22. E71T1-C1A4-CS1 (58) (70~95) ( 20ft lbs at -40 ). v Chemical Analysis of the weld metal(wt%). Brand Name C Si Mn P S.

6 Supercored 71H AWS E71T1-C1A4-CS1. This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI . welding CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure, shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements.

7 Supercored 71H. welding Efficiency v Deposition Rate & Efficiency welding Wire Feed Deposition Deposition Consumable Conditions Speed Efficiency Rate (size). Amp.(A) Volt.(V) m/min (in/min) % kg/hr(lb/hr). 200 26 (400) 85~86 ( ). Supercored 71H. 250 28 (450) 86~87 ( ). ( ). 300 33 (600) 87~88 ( ). 250 28 (300) 85~86 ( ). Supercored 71H. 300 32 (400) 87~88 ( ). ( ). 330 36 (500) 87~88 ( ). Deposition Deposition rate efficiency =(Deposited metal =(Deposited metal Remark weight/. weight/. welding Wire weight time,min.) 60. used) 100. * Shielding Gas : 100%CO2.

8 This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI . welding CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure, shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements.

9 Supercored 71H. Diffusible Hydrogen Content v welding Conditions Diameter : ( ) Amps(A) / Volts(V) : 240A / 27V. Shielding Gas : 100%CO2 20~25mm Stick-Out(mm) : ( ~ ). Flow Rate : 20 /min 30 cm/min welding Position : 1G (PA) welding Speed : (12 in/min). Current Type & Polarity : DC(+). v Hydrogen Analysis Using Gas Chromatograph Method Hydrogen Evolution Time : 72 hrs Evolution Temp. : 45 (113 ). Barometric Pressure : 780 mm-Hg v Result( /100g Weld Metal). X1 X2 X3 X4. Average Hydrogen Content / 100g Weld Metal This information is provided solely for the purpose of confirming product conformance with applicable standards.

10 The serviceability of a product or structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI . welding CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure, shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements. Supercored 71H. Proper welding Condition v Proper Current Range Wire Dia. Shielding welding consumables Gas Position ( ) ( ) (1/16in).