TECHNICAL DATA SHEET HIGH DENSITY POLYETHYLENE …

1 TECHNICAL DATA SHEET . high DENSITY POLYETHYLENE (HDPE) sheathing compound . HDP 333 UV Black (CACT Approved). _____. DESCRIPTION: HDP- 333 UV Black is a high - DENSITY POLYETHYLENE (HDPE) compound developed to be used for sheathing of Fiber Optic Cables (OFC) / PIJF & Power cables. It has been formulated with necessary additives and processing aid to achieve good extrusion. The incorporation of of Carbon black gives the UV and light stabilization required for the compound and the cables it is used on. APPLICATIONS: HDP 333 UV is suitable for sheathing of Optic Fibre Cables (OFC) / PIJF / Power cables. SL. PARAMETERS UNIT TEST METHOD TEST VALUE. No 01 DENSITY * Gm/cc BS-6234 / ASTM D 1505 02 MFI* Gm/10 min ASTM D 1238 < 03 OIT Min BS 6234 / ASTM D 3895 Greater than 35.

2 04 TENSILE STRENGTH @ Kg/Sq mm ASTM D 1238 > BREAK. 05 ELONGATION @ BREAK % ASTM D 1238 >600. 06 ESCR - ASTM D 1693 48 Hours No Failure 07 Carbon Black Content ------ - %. 08 Carbon Black dispersion - ------ Good Dispersion 09 DIELECTRIC CONSTANT - ASTM D 1531 / 150 10 DISSIPATION FACTOR - ------- 11 VOLUME RESISTIVITY Ohm-cm - ASTM D 257------ x 1015. 12 RELATIVE PERMITIVITY - ------- 13 MOISTURE CONTENT % ------- * Note: Based on DENSITY of base Raw Material. The compound is also available in Orange / Blue / Red & Green colors also. PACKING: The product is packed in HDPE laminated woven bags weighing 25 Kg. NOTE: The above test results are based on standard tests and should be used only as a guideline.

3 The performance depends on different conditions of processing & fabrication and users are advised to establish for themselves that the material supplied meets the requirement to their satisfaction. TECHNICAL DATA SHEET . high DENSITY POLYETHYLENE (HDPE) INSULATION compound . GRADE - HDP 666 (CACT Approved). _____. DESCRIPTION: HDP 666 is HDPE based compound is developed to be used for insulation of JFT cables. It has been formulated with necessary additives and processing aid to achieve good extrusion, speed etc. APPLICATIONS: HDP 666 is suitable for insulation of Copper cables. PROPERTIES OF UNIT TEST TYPICAL. compound METHOD VALUES. BS-6234 /. DENSITY * gm / cc ASTM D 1505 to MFI gm / 10 Min ASTM D < 1238.

4 OIT (Aluminium Pan) Minutes BS 6234 / >60 min. ASTM D 3895. ESCR No Cracks ASTM D 1693 No Cracks 48 Hours Tensile Strength ASTM D 1238 160 kg/cm2. Elongation at Break. % ASTM D 1238 > 400 %. Dissipation Factor ---- Measured @ 1 MHz Max Volume Resistivity Ohm-cm ASTM D 257 1 X 1015. Dielectric Constant ---- ASTM D 1531 / 150 Max Brittleness Temperature Max ASTM D 746 - 550 C. Thermal Stress Cracking - ASTM D 2951 No Cracks Di-electric strength KV, DC ASTM D 149 20 KV, DC / mm * Note: Based on DENSITY of base Raw Material. PACKING: The product is packed in HDPE laminated woven bags weighing 25 Kg. NOTE: The above test results are based on standard test and should be used only as a guideline.

5 The performance depends on different conditions of processing, fabrication and users are advised to establish for themselves that material supplied meet the requirement to their satisfaction. TECHNICAL DATA SHEET . LENIER LOW DENSITY POLYETHYLENE (LLDPE) compound . GRADE LLP 222 (CACT Approved). _____. DESCRIPTION: LLP-222 is a black linier low- DENSITY POLYETHYLENE compound developed for sheathing of Jelly filled telephone cables. It is formulated to give excellent finish and good ESCR properties. Well-dispersed carbon black makes the product weather and ultraviolet radiation resistant. APPLICATION: LLP - 222 is suitable for sheathing of Jelly filled telecom cable. PROPERTIES OF UNIT TEST TYPICAL VALUE.

6 compound METHOD. DENSITY * Gm / cc BS-6234 / ASTM D to 1505. MFI Gm / 10 ASTM D 1238 - Min OIT Minutes BS 6234 / ASTM D >30 Min. 3895. Carbon Black Content % ------ - Carbon Black dispersion - ------ Good Dispersion Tensile Strength at break N/Sq. mm ASTM D 1238 18. Elongation at break % ASTM D 1238 500. Tensile Strength at yield N/Sq. mm ASTM D 1238 11. ESCR (50o C , 10% Igepal) >48 Hours ASTM D 1693 48 No Failure. Hours Shrinkage <5% length 2%. wise Dielectric strength 20 KV DC ASTM D 149 25. * Note: Based on DENSITY of base Raw Material. PACKING: The product is packed in HDPE laminated woven bags weighing 25 Kg. NOTE: The above test results are based on standard test and should be used only as a guideline.

7 The performance depends on different conditions of processing fabrication and users are advised to establish for themselves that material supplied meet the requirement to their satisfaction. TECHNICAL DATA SHEET . MEDIUM DENSITY POLYETHYLENE (MDPE) compound . GRADE - MDPE 777 ( sheathing ). _____. DESCRIPTION: MDP - 777 is a Black Medium DENSITY POLYETHYLENE compound developed for sheathing of Power Cables ABC Conductors & Jelly filled telephone cables. It is formulated to give excellent finish and good ESCR. properties. Well-dispersed carbon black makes the product weather and ultraviolet radiation resistant. APPLICATION: MDP - 777 is suitable for sheathing of Power Cables, ABC Conductors & Jelly filled telecom cable.

8 The compound confirms to BS 6234 Type 03C: TS2, EN 50290-2-4 & IEC 60840, Type ST3 & ST7. PROPERTIES OF UNIT TYPICAL VALUE. compound TEST METHOD. DENSITY * Gm / cc BS-6234 / ASTM D 1505 to MFI Gm / 10 Min ASTM D 1238 - OIT Minutes BS 6234 / ASTM D 3895 >30 Min. Carbon Black Content % ------ - Carbon Black dispersion - ------- Good Dispersion Tensile Strength at break N/Sq. mm ASTM D 1238 >18. Elongation at break % ASTM D 1238 >600. Tensile Strength at yield N/Sq. mm ASTM D 1238 >10. ESCR (50o C , 10% Igepal) >48 Hours ASTM D 1693 48 Hours No Failure. Shrinkage <5% length ------- 2%. wise Dielectric strength 20 KV DC ASTM D 149 25. * Note: Based on DENSITY of base Raw Material.

9 PACKING: The product is packed in HDPE laminated woven bags weighing 25 Kg. NOTE: The above test results are based on standard test and should be used only as a guideline. The performance depends on different conditions of processing fabrication and users are advised to establish for themselves that material supplied meet the requirement to their satisfaction. TECHNICAL DATA SHEET . high DENSITY POLYETHYLENE (HDPE) sheathing compound . HDP 333 UV Orange / Red / Blue / Green _____. DESCRIPTION: HDP- 333 UV Black is a high - DENSITY POLYETHYLENE (HDPE) compound developed to be used for sheathing of Fiber Optic Cables (OFC) / PIJF & Power cables. It has been formulated with necessary additives and processing aid to achieve good extrusion.

10 The compound is incorporated with the required and necessary UV and Light stabilization additives to protect against UV degradation. APPLICATIONS: HDP 333 UV is suitable for sheathing of Optic Fibre Cables (OFC) / PIJF / Power cables. SL. PARAMETERS UNIT TEST METHOD TEST VALUE. No 01 DENSITY * Gm/cc BS-6234 / ASTM D 1505 02 MFI* Gm/10 min ASTM D 1238 < 03 OIT Min BS 6234 / ASTM D 3895 Greater than 35. 04 TENSILE STRENGTH @ Kg/Sq mm ASTM D 1238 > BREAK. 05 ELONGATION @ BREAK % ASTM D 1238 >600. 06 ESCR - ASTM D 1693 48 Hours No Failure 07 UV RESISTANCE - IEC 60068-2-5 Passes 08 DIELECTRIC CONSTANT - ASTM D 1531 / 150 09 DISSIPATION FACTOR - ------- 10 VOLUME RESISTIVITY Ohm-cm - ASTM D 257------ x 1015.