Technical Data Sheet - McCoy Soudal

1 Technical data SheetFIRESILICONE B1 FRDate:17/03/06 Page 1 of 2 Remark: The directives contained in this documentation are the result of our experiments and of our experience and have been submitted in good of the diversity of the materials and substrates and the great number of possible applications which are out of our control, we cannot accept anyresponsability for the results obtained. In every case it is recommended to carry out preliminary NV Everdongenlaan 18-20 2300 Turnhout, BelgiumTel.: +32 (0) : +32 (0) data :BasePolysiloxaneConsistencyStable PastaCuring SystemMoisture CureSkin FormingCa 20 min.

2 (20 C/65% )Curing Rate1mm/24hShore A Hardness16 Shore ASpecific GravityCa 1,17g/cm Temperature Resistance-40 C until +140 CElongation at Break900% (DIN52455)E-Modulus 100%0,20N/mm (DIN52455)Elastical Recovery>90% (DIN52455)Maximum Deformation 25%Product:Firesilicone B1 FR is a high quality, neutral, elastic,one-component sealant based on silicones whichconforms to the DIN4102 B1 standard for fireretardancy and has a fire rating of up to 4 hours incertain joint configurations (EN 1366 Part 4 BS 476/20).Characteristics:- Very easy to apply- Colourfast and UV-resistant- Remains permanently elastic after full cure- Very good adhesion on most surfaces- Low modulus- DIN 4102-Part 2: Class B1- Up to 4 hours fire rating with normal PEbacking material (see table enclosed)Applications:All building and glazing joints which require a fireratingFire rated expansion jointsPackaging:Colour: grey, whitePackaging: cartridge 310mL, foil bag 600mLShelflife.

3 9 months in unopened packaging in a cool and drystorage place at temperatures between +5 C and+25 . Do not expose to :Type: all usual porous and non-porous buildingmaterialsState of Surface: clean, dry, free of dust and greasePreparation: porous substrates should be primedwith Primer 150. Soudal Surface Activator willimprove adhesion on smooth recommend a preliminary compatibility Size:Minimum Width: 5mmMaximum Width: 30mmJoint configuration: width = 2x depthApplication:Method: caulking gunBacking material: PE backer rods for correct jointdimensionApplication temperature: +1 C to +30 CClean: with white spiritRepair: with Firesilicone B1 FRFinish: with soapy solutionHealth- and Safety Recommendation:Apply the usual industrial data SheetFIRESILICONE B1 FRDate:17/03/06 Page 2 of 2 Remark.

4 The directives contained in this documentation are the result of our experiments and of our experience and have been submitted in good of the diversity of the materials and substrates and the great number of possible applications which are out of our control, we cannot accept anyresponsability for the results obtained. In every case it is recommended to carry out preliminary NV Everdongenlaan 18-20 2300 Turnhout, BelgiumTel.: +32 (0) : +32 (0) : Test Report 9297 University of Ghent to NBN EN 1366-4 BS 476:Part 20 Warrington Fire ResearchReport DIN4102-B1 Institut f r Bautechnik, Berlin TNO-rapport 2000-CVB-R00703 Test Results Test Report 9297:Wall ThicknessWidth of JointDepth of JointApplicationFire Rating100mm11mm10mmDoublesided146 min.

5 TIRating EI 120202 min. FRRating E 180100mm33mm20mmDoublesided116 min. TIRating EI 90187 min. FRRating E 180200mm11mm10mmDoublesided>240 min. TI>240 min. FRRating EI 240200mm31mm20mmDoublesided225 min TIRating EI 180>240 min. FRRating E 240TI = Thermal Insulation; the time during which the temperature on the unexposed side of the wall does not rise by morethan 180 CFR = Flame Resistance; the time during which the joints stops flames from penetrating the wallFire Rating: Draft European Commission Decision RG N170