VALOX™ FR Resin 357 - Sabic工程塑胶原料, Lexan …

1 Revision 20170913 VALOX FR Resin 357 REGION AMERICASDESCRIPTIONPBT+PC, UL94V-0/5VA Rated, Impact Modified, Opaque, Unreinforced. Applications like bobbins, switches and PROPERTY VALUESPROPERTIESTYPICAL VALUESUNITSTEST METHODSMECHANICALT ensile Stress, yld, Type I, 50 mm/min48 MPaASTM D 638 Tensile Stress, brk, Type I, 50 mm/min42 MPaASTM D 638 Tensile Strain, yld, Type I, 50 mm/min5%ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min54%ASTM D 638 Tensile Modulus, 5 mm/min2020 MPaASTM D 638 Flexural Stress, yld, mm/min, 50 mm span78 MPaASTM D 790 Flexural Stress, brk, mm/min, 50 mm span78 MPaASTM D 790 Flexural Modulus, mm/min, 50 mm span2100 MPaASTM D 790 Hardness.

2 Rockwell R117-ASTM D 785 Tensile Stress, yield, 50 mm/min50 MPaISO 527 Tensile Stress, break, 50 mm/min40 MPaISO 527 Tensile Strain, yield, 50 mm/min5%ISO 527 Tensile Strain, break, 50 mm/min30%ISO 527 Tensile Modulus, 1 mm/min2200 MPaISO 527 Flexural Stress, yield, 2 mm/min73 MPaISO 178 Flexural Modulus, 2 mm/min2000 MPaISO 178 IMPACTIzod Impact, unnotched, 23 CNB3204J/mASTM D 4812 Izod Impact, notched, 23 C319J/mASTM D 256 Izod Impact, notched, -30 C153J/mASTM D 256 Gardner, 23 C43 JASTM D 3029 Modified Gardner, 23 C43 JASTM D 3029 Instrumented Impact Total Energy, 23 C35 JASTM D 3763 Izod Impact, notched 80*10*4 +23 C45kJ/m ISO 180/1 AIzod Impact, notched 80*10*4 -30 C10kJ/m ISO 180/1 ACharpy 23 C, V-notch Edgew 80*10*4 sp=62mm45kJ/m ISO 179/1eATHERMAL 2017 Copyright by SABIC.

3 All rights reservedVicat Softening Temp, Rate B/50134 CASTM D 1525 HDT, MPa, mm, unannealed135 CASTM D 648 HDT, MPa, , unannealed98 CASTM D 648 HDT, MPa, mm, unannealed138 CASTM D 648 HDT, MPa, mm, unannealed99 CASTM D 648 CTE, -40 C to 40 C, CASTM E 831 CTE, -40 C to 40 C, CASTM E 831 CTE, 60 C to 138 C, CASTM E 831 CTE, -40 C to 40 C, CISO 11359-2 CTE, -40 C to 40 C, CISO 11359-2 Ball Pressure Test, 125 C +/- 2 C, by VDEPASSES-IEC 60695-10-2 Vicat Softening Temp, Rate B/50145 CISO 306 Vicat Softening Temp, Rate B/120150 CISO 306 HDT/Af, MPa Flatw 80*10*4 sp=64mm84 CISO 75/AfRelative Temp Index, Elec120 CUL 746 BRelative Temp Index, Mech w/impact120 CUL 746 BRelative Temp Index, Mech w/o impact140 CUL 746 BPHYSICALS pecific D 792 Specific /gASTM D 792 Water Absorption, 24 D 570 Mold Shrinkage, flow, mm (5)1 methodMold Shrinkage, flow, mm (5) methodMold Shrinkage, flow, mm (5)1 methodMold Shrinkage, xflow, mm (5) methodMold Shrinkage, xflow, mm (5)

4 MethodMelt Flow Rate, 250 minASTM D ISO 1183 Water Absorption, (23 C/sat) 62 Moisture Absorption (23 C / 50% RH) 62 Melt Volume Rate, MVR at 250 kg8cm /10 minISO 1133 ELECTRICALV olume Resistivity> +16 Ohm-cmASTM D 257 Dielectric Strength, in air, D 149 Dielectric Strength, in oil, D 149 Dielectric Strength, in oil, D 149 Relative Permittivity, 100 D 150 Relative Permittivity, 1 D 150 PROPERTIESTYPICAL VALUESUNITSTEST METHODS 2017 Copyright by SABIC. All rights reservedDissipation Factor, 100 D 150 Dissipation Factor, 1 D 150 Arc Resistance, Tungsten {PLC}6 PLC CodeASTM D 495 Hot Wire Ignition {PLC)2 PLC CodeUL 746 AHigh Voltage Arc Track Rate {PLC}3 PLC CodeUL 746 AHigh Ampere Arc Ign, surface {PLC}3 PLC CodeUL 746 AComparative Tracking Index (UL) {PLC}2 PLC CodeUL 746 AFLAME CHARACTERISTICSUL Recognized, 94HB Flame Class Rating (3) 94UL Recognized, 94V-0 Flame Class Rating (3) 94UL Recognized, 94-5VA Rating (3)3mmUL 94 Oxygen Index (LOI)}

5 30%ASTM D 2863 Glow Wire Flammability Index 960 C, passes at1mmIEC 60695-2-12 Glow Wire Ignitability Temperature, mm775 CIEC 60695-2-13 Glow Wire Ignitability Temperature, mm750 CIEC 60695-2-13 Glow Wire Ignitability Temperature, mm725 CIEC 60695-2-13UV-light, water exposure/immersionF2-UL 746 CINJECTION MOLDINGD rying Temperature120 CDrying Time3 4hrsDrying Time (Cumulative)12hrsMaximum Moisture Temperature250 265 CNozzle Temperature245 260 CFront - Zone 3 Temperature250 265 CMiddle - Zone 2 Temperature245 260 CRear - Zone 1 Temperature240 255 CMold Temperature50 75 CBack Speed50 100rpmShot to Cylinder Size40 80%Vent VALUESUNITSTEST METHODS 2017 Copyright by SABIC.

6 All rights reservedDISCLAIMERAny sale by SABIC, its subsidiaries and affiliates (each a seller ), is made exclusively under seller s standard conditions of sale(available upon request) unless agreed otherwise in writing and signed on behalf of the seller. While the information contained hereinis given in good faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY ANDNONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECTTO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANYAPPLICATION.

7 Each customer must determine the suitability of seller materials for the customer s particular use through appropriatetesting and analysis. No statement by seller concerning a possible use of any product, service or design is intended, or should beconstrued, to grant any license under any patent or other intellectual property right. 2017 Copyright by SABIC. All rights reserv