VITON® Fluorelastomers An overview - Rubber Technology
Hardness IRHD ± 5° DIN 53519 70 70 90 75 90 80 75 Tensile strength Mpa.min. DIN 53504 13 12 14 14 18 11 10,7 Elongation % DIN 53504 170 170 120 224 121 130 213 Compression set % 24h/200°C on slab max. DIN 53517 12 14 14 10 117 15 4,6 on O-R 3.53 mm max. 18 19 18 11 20 7,5 Heat aging 70h/200°C
Tags:
Information
Domain:
Source:
Link to this page:
Related documents
Physical Properties - Plastics & Rubber
plastics-rubber.basf.comThe hardness of elastomers such as Elastollan® is measured in Shore A and Shore D according to DIN ISO 7619-1 (3s). Shore hardness is a measure of the resistance of a material to the penetration of a needle under a defined spring force. It is determined as a number from 0 to 100 on the scales A or D. The higher the number, the higher the hardness.
Characteristic properties of Silicone Rubber Compounds
www.shinetsusilicone-global.comHardness Change in hardness KE-7611 KE-951 KE-551 Weatherability ... Silicone rubber can be immersed in water (cold water, warm water, boiling water) for long periods with water absorption of about 1%, and with virtually no effect on mechanical strength or electrical properties. Typically, under ordinary pressure, contact with steam causes
Copy of Rubber Band Size Chart
www.rubberband.comAfter a rubber band has been stretched, it will typically come to rest at a longer length than before it was stretched. This is expressed as a percent of the original length of the band. ¬ The ratio of the density (weight) of a substance to the density of water. ¬ Measure of the hardness of non-metallic materials or "resistance to identation."
Silicone Rubber -Performance Test Results-
www.shinetsusilicone-global.comHardness Durometer A 50 54 52 53 54 58 45 40 51 Tensile strength MPa 6.6 7.7 9.3 7.7 11.0 9.2 2.5 7.4 8.8 Elongation at break % 310 450 730 520 780 680 320 680 400 kN/m 6 15 38 19 31 35 8 26 22 3 Compression set 180°C x 22 h 8 20 13 22 9 10 …
Types, Properties & Uses of Hypalon
www.inforubber.comHardness, Durometer A 45–95 60–95 65–98 40–95 Tensile Strength, MPa Carbon Black Stocks Up to 20 Up to 24 Up to 27 Up to 27 ... rubber are extremely resistant to attack by ozone, oxygen and weather. In addition, properly prepared vulcanizates of Hypalon ...
REPAIR CATALOG - Vibram US
us.vibram.com• Softness, which is defined as hardness. Vibram compounds offer a wide range of hardness levels. All levels have excellent wear resistance. Compound Suggested Adhesive Hardness (shoreA) Abrasion SBR (359 cmpd) Neoprene 70-80 150 min NBS Fire & Ice Urethane 57-67 120 min NBS TC4 Neoprene 55-65 120 min NBS TC1 Neoprene 55-65 120 min NBS
Rubber Material Selection Guide NBR / Nitrile or Buna N ...
www.robinsonrubber.comformulate a NBR or nitrile / buna n rubber compound to meet your specific application and performance requirements, please contact Robinson Rubber Products at e-mail: sales@robinsonrubber.com or phone: +1-763-535-6737. Robinson Rubber Products Company, Inc. makes no expressed or implied warranty as to any qualities, attributes, or