TECHNICAL DATA SHEET - PPG AEROSPACE
Stir the topcoat slowly during the application. The suggested film thickness is 50 to 100 microns (2.0 to 4.0 mils). For gloss and semi-gloss topcoats this can be accomplished by two or three medium coats with a 50% overlap. With the flat and gunship/matte coatings it may be
Tags:
Sheet, Data, Technical, Technical data sheet, Topcoat
Information
Domain:
Source:
Link to this page:
Please notify us if you found a problem with this document:
Documents from same domain
Desothane® HS CA8800 Polyurethane Topcoats
www.ppgaerospace.com50 - 100 minutes 90 hours 7 -10 hours 25 40 40 60 65 hours CA8800CT2 4 - 5 hours 15 - 30 minutes 35 - 45 minutes 40 hours CA8800CT3 3 - 4 hours 10 - 15 minutes 30 - 40 minutes 24 hours 2 -3 hours 5 10 15 20 12 hours CA8800CT5 1 – 2 hours 3 – 5 minutes 10 – 15 minutes 8 hours 25°C (77°F)
Global Military Coatings Guide - PPG AEROSPACE
www.ppgaerospace.comsupply of coatings products for the military aerospace segment of the industry. PPG has a full line of topcoats and primers needed for the industry supporting fighters, trainers, transport aircraft, and helicopters. Our Advanced Performance Coatings have become the industry standard supporting nearly all platforms in the industry.
TECHNICAL DATA SHEET
www.ppgaerospace.com513 X 419 Page 1 DeSoto® 513X419 Military Epoxy Polyamide Primer TECHNICAL DATA SHEET Product Description DeSoto® 513X419 military epoxy primer is a high solids, chemical and solvent resistant coating. It is used over aluminum and composite surfaces prior to top coating. Compatible with Desothane® HS topcoats Excellent adhesion and corrosion resistance
Commercial and General Aviation Coatings Guide
www.ppgaerospace.comPPG Aerospace, PRC-DeSoto is qualified to more Commercial and General Aviation specifications than any other supplier. With more than a thousand types of coatings, we offer the industry’s
Technical Data Sheet - Aerospace
www.ppgaerospace.comTechnical Data Sheet Aerospace Sealants PR-1440 Class B fuel tank sealant Description PR-1440 Class B is an aircraft integral fuel tank sealant. It
Technical Data Sheet - PPG AEROSPACE
www.ppgaerospace.comthixotropic paste suitable for application by extrusion gun or spatula. It cures at room temperature to form a resilient sealant having excellent adhesion to common aircraft substrates. The following tests are in accordance with AMS-S-8802 Class B specification test methods. Application properties (typical) Color part A black part B off white
TECHNICAL DATA - PPG AEROSPACE
www.ppgaerospace.comextrusion gun or spatula. Unlike standard polysulfide fuel tank sealants, it can cure at low temperatures and is unaffected by changes in relative humidity. This sealant has excellent adhesion to common aircraft substrates when correctly primed with PR-1826AP Adhesion Promoter. The following tests are in accordance with AMS 3277
TECHNICAL DATA SHEET
www.ppgaerospace.comEpoxy Primer Health Precautions This product is safe to use and apply when recommended precautions are followed. Before using this product, read and understand the Safety Data Sheet (SDS), which provides information on health, physical and environmental hazards, handling precautions and first aid recommendations. An SDS is available on request ...
Commercial and General Aviation Coatings Guide
www.ppgaerospace.comDassault/Falcon France 5 DHMS C4.01 Canada 2 DHMS C4.04 Canada 7, 8, 18 DHMS C4.06 Canada 15 DHMS C4.18 Canada 2 DMS 1786 USA 1 DMS 1850 USA 15 DMS 2104 USA 2 DMS 2143 USA 7 DMS 2144 USA 2 DMS 2433 USA 12 DPM 4838 USA 1 DPM 5391 USA 11 DPM 5893 USA 14 DPM 6456 USA 7, 18 DPM 6546 USA 7, 18 DPM 6568 USA 4 DPM 8226 USA 19
MIL-PRF-85285 TYPE I CLASS H - ppgaerospace.com
www.ppgaerospace.comPRODUCT INFORMATION DATA SHEET 17451 Von Karman Avenue, Irvine, CA 92614 Tel (949) 474-0400 (800) 544-3338 . Fax (949) 474-7269 . www.deftfinishes.com
Related documents
FY-22CH-1 21FEB2021
www.navsea.navy.miltopcoat; for materials to be installed in all other areas, they must be blasted and coated at a maximum 85 percent relative humidity; this requirement supersedes Notes (26) and (29A). 3.1.4.1 For tanks, when masking is removed from the open ends of piping, the piping may retain tightly-adherent paint or remain bare up to 6 inches above the open