EOS Aluminium AlSi10Mg Material Data Sheet
HCF, ASTM E466-15, 20 million cycles, fully reversed High cycle fatigue testing performed on machined vertical and horizontal samples. No heat treatment. Aluminum alloys do not have fatigue limit. Actual fatigue values depend on sample geometry and specially surface finish. Fatigue strength Typical lower limit of fatigue strength
Tags:
Information
Domain:
Source:
Link to this page:
Documents from same domain
EOS StainlessSteel 316L Material Data Sheet
www.eos.infoMechanical Properties as manufactured Mechanical properties ISO6892-1 Yield strength R p0.2 [MPa] Tensile strength R m [MPa] Elongation at break A [%] Number of samples Vertical 480 570 51 105 Horizontal 540 640 40 90 Yield strength [R pO.2] Tensile strength [R m] Elongation [A] Vertical Horizontal 750 700 650 600 550 500 450 400 80 % 60 % 40 % ...
EOS NickelAlloy IN718 Material Data Sheet
www.eos.infoAverage defect percentage 0.03 % 10 Density, ISO3369 Result Number of samples Average density min 8.15 g/cm3 10 Chemical and Physical Properties of Parts 50 µm Heat treated microstructure. Etched according to ASTM E407-07. System set-up EOS M 290 EOS material set IN718 Performance 2.0 EOSPAR name IN718_040_PerformanceM291_2xx Software …
Related documents
Fatigue Analysis - UTEP
me.utep.edu•Low Cycle Fatigue (LCF) - when N f is in the range of 100 to 103. •High Cycle Fatigue (HCF) - when the number of Cycles to failure, N f, is in the range of 103 to 106. •Infinite Life - when N f is equal to or greater than 106.
High-Temperature Materials Testing Solutions
www.mts.comto develop the next generation of ultra-efficient aircraft, automobiles and power generation systems, researchers worldwide turn to mts for high-temperature materials testing solutions.