GRILON TSG-35/4 - kphuaxun.com

1 TECHNICAL DATA SHEETGRILON TSG-35/4 GRILON TSG-35/4 is a heat stabilised, normalviscosity PA66 + PA6 injection mouldinggrade with 35% glass TSG-35/4 has the following importantproperties: Good flow behaviour Good surface finish Easy processingApplication examples are stressed functionalparts such as wheels, electrical bobbins,handles and PropertiesStandardUnitStateGrilonTSG-35/ 4 Tensile E-Modulus1 mm/minISO strength at break5 mm/minISO at break5 mm/minISO 527% strengthCharpy, 23 CISO 179/2-1 strengthCharpy, -30 CISO 179/2-1 impact strengthCharpy, 23 CISO 179/2-1 impact strengthCharpy, -30 CISO 179/2-1 indentation hardnessISO PropertiesMelting pointDSCISO 11357 Cdry260 Heat deflection temperature MPaISO 75 Cdry240 Heat deflection temperature MPaISO 75 Cdry175 Thermal expansion coefficient CISO 1135910-4 expansion coefficient CISO 1135910-4 usage temperaturelong termISO 2578 Cdry90 - 110 Maximum usage temperatureshort termISO 2578 Cdry200 Electrical PropertiesDielectric strengthIEC 60243-1 tracking indexCTIIEC volume resistivityIEC 60093 surface resistivityIEC 60093 PropertiesDensityISO 1183 (UL94) mmISO 1210rating-HBWater absorption23 62%-5 Moisture absorption23 C/50% 62%-2 Linear mould 294% mould 294% acc.

2 ISO 1874:PA66+PA6, MHR, 14-110N, GF353 Processing information for the injection moulding of GRILON TSG-35/4 This technical data sheet for GRILON TSG-35/4 pro-vides you with useful information on material prepa-ration, machine requirements, tooling and PREPARATIONG rilon TSG-35/4 is delivered dry and ready forprocessing in sealed, air tight packaging. Predryingis not necessary provided the packaging is , undamaged bags can be kept over a longperiod of time in storage facilities which are dry,protected from the influence of weather and wherethe bags can be protected from and safetyDetailed information can be obtained from the material Safety Data Sheet (MSDS) which can berequested with every material TSG-35/4 is dried and packed with a mois-ture content of %.

3 Should the packagingbecome damaged or be left open too long, then thematerial must be dried. A too high moisture contentcan be shown by a foaming melt, excessive nozzledrool and silver streaks on the moulded can be done as follows:Temperature:max. 80 CTime:4 - 12 hoursDew point of the dryer:-25 CTemperature:max. 100 CTime:4 - 12 hoursDrying timeIf there is only little evidence of foaming of the meltor just slight silver streaks on the part, then theabove mentioned minimal drying time will be suffi-cient. If material is stored open for days, showsstrong foaming, unusually easy flow, streaks or arough surface on the moulded part, then the maxi-mum drying time is streaks can also be caused byoverheating of the material (over 350 C)or by too long melt residence time in temperaturePolyamides are affected by oxidation at tempera-tures above 80 C in the presence of oxygen.

4 Visibleyellowing of the material is an indication of oxida-tion. Hence temperatures above 80 C for desiccantdryers and temperatures above 100 C for vacuumovens should be avoided. In order to detect oxida-tion it is advised to keep a small amount of granu-late (light colour only !) as a comparison longer residence times (over 1 hour) hopperheating or a hopper dryer (80 C) is of regrindGrilon TSG-35/4 is a thermoplastic material . Hence,incomplete mouldings as well as sprues and run-ners can be reprocessed. The following pointsshould be observed: Moisture absorption Grinding: Dust particles and particle size distri-bution Contamination through foreign material , dust,oil, etc. Level of addition to original material Colour variation Reduction of mechanical propertiesWhen adding regrind, special care has to be takenby the REQUIREMENTSG rilon TSG-35/4 can be processed economicallyand without problems on all machines suitable protected, universal screws with shut-offnozzles are recommended (3 zones).

5 Length:18 D - 22 DCompression ratio:2 - volumeThe metering stroke (less decompression distance)must be longer than the length of the volume = - x(max. shot volume of injection unit)ScrewSelecting the injection unit!Desiccant dryerVacuum oven4 HeatingAt least three separately controllable heatingzones, capable of reaching cylinder temperaturesup to 350 C. Separate nozzle heating is neces-sary. The cylinder flange temperature must becontrollable (cooling).NozzleOpen nozzles are simple, allow an easy melt flowand are long lasting. There is however, the dangerthat during retraction of the screws following injec-tion of the melt, air maybe drawn into the barrel(decompression). For this reason, needle shut-offnozzles are often forceAs a rule of thumb the clamping force can be esti-mated using the following formula:TOOLINGThe design of the mould tool should follow thegeneral rules for glass fibre reinforced the mould cavities common mould tool steelquality ( hardened steel) which has been hard-ened to level of 56 HRC is necessary.

6 We recom-mend additional wear protection in areas of highflow rates in the tool ( pin point gates, hot run-ner nozzles).Demoulding / Draft angleAsymmetric demoulding and undercuts are to beavoided if possible. Generous provision should bemade for ejection with many large pins or a stripperplate. Draft angles for the inner and outer wall be-tween and 3 is usually sufficient. Texturedsurfaces require a larger draft angle (1 per depth of roughness).(VDI 3400)121518212427 Depth of roughness ( m) angle (%) (VDI 3400)303336394245 Depth of roughness ( m) angle (%) and runnerTo achieve the best mould filling and avoid sinkmarks, a central gate at the thickest section of themoulding is recommended. Pin point (direct) ortunnel gates are more economical and more com-mon with technical avoid premature solidification of the melt anddifficult mould filling, the following points should beconsidered: x thickest wall section of the injectionmoulding part x thickest wall section of the injectionmoulding part (but minimum 4 mm)VENTINGIn order to prevent burning marks and improveweld line strength, proper venting of the mouldcavity should be provided (venting channels on theparting surface dimensions: Depth mm, width2 - 5 mm).

7 PROCESSINGM ould filling, post pressure and dosingThe best surface finish and a high weld linestrength are achieved when a high injection speedand a sufficiently long post pressure time are injection speed should be regulated so as toreduce towards the end of the filling cycle in orderto avoid burning. For dosing at low screw revolu-tions and pressure the cooling time should be machine settingsIn order to start up the machine for processingGrilon TSG-35/4 , the following basic settings can berecommended:Flange60 - 80 CZone 1270 CZone 2275 CZone 3280 CNozzle275 CTool80 - 100 CMelt280 - 300 CInjection speedmedium - highHold-on pressure (spec.) 300 - 800 barDynamic pressure (hydr.) 5 - 15 barScrew speed50 - 100 kN1) x projected area (cm2)1) for a cavity pressure of 750 barClamping forceGate diameterRunner diameterTemperaturesPressures / Speeds5 CUSTOMER SERVICESEMS-GRIVORY is a specialist in polyamide synthe-sis and the processing of these materials.

8 Our cus-tomer services are not only concerned with themanufacturing and supply of engineering thermo-plastics but also provide full technical support in-cluding: Rheological design calculation / FEA Prototype tooling material selection Processing support Mould and component designWe are happy to advise you. Simply call one of oursales recommendations and data given are based on ourexperience to date, however, no liability can be assumedin connection with their usage and