NOT MEASUREMENT SENSITIVE SUPERSEDING …

1 NOT MEASUREMENT SENSITIVE MIL-DTL-13924D 18 March 1999 SUPERSEDING MIL-C-13924C 9 June l980 DETAIL SPECIFICATIONCOATING, OXIDE, BLACK, FOR FERROUS METALS This specification is approved for use by all Departments and Agencies of the Department of Defense. 1. SCOPE Scope. This specification covers black oxide coatings applied to ferrousmetals (wrought iron, carbon, low alloy, and corrosion resistant steels).

2 Blackoxide coatings, with or without a supplementary preservative treatment (see ),may be used where a black surface is required. Only very limited corrosionprotection, under mildly corrosive conditions, is obtained as a result of blackoxide coating (see ). Black coatings are included in this specification withlimitations as noted in Classification. Black oxide coatings covered by this specification should beof the following classes as specified (see and ). Class 1 Alkaline oxidizing process (for wrought iron, cast and malleableirons, plain carbon, and low alloy steels).

3 Class 2 Alkaline chromate oxidizing process (for use on certain corrosionresistant steel alloys which are tempered at less than 900 F (482 C)). Class 3 Fused salt oxidizing process (for corrosion resistant steel alloyswhich are tempered at 900 F (482 C) or higher). Class 4 Alkaline oxidizing process (for other corrosion resistant steelalloys).Beneficial comments (recommendations, additions, deletions) and any pertinent datawhich may be of use in improving this document should be addressed to: Director, Army Research Laboratory, Weapons and Materials Research Directorate,ATTN: AMSRL-WM-M, Aberdeen Proving Ground, MD 21005-5069 by using theStandardization Document Improvement Proposal (DD Form 1426) appearing at the endof this document or by N/A AREA MFFPMIL-DTL-13924D2 2.

4 APPLICABLE DOCUMENTS General. The documents listed in this section are specified in sections 3and 4 of this specification. This section does not include documents in othersections of this specification or recommended for additional information or asexamples. While every effort has been made to ensure the completeness of this list,document users are cautioned that they must meet all specified requirementsdocuments cited in sections 3 and 4 of this specification, whether or not they arelisted. Government documents.

5 Specifications, standards, and handbooks. The following specifications,standards, and handbooks form a part of this document to the extent specifiedherein. Unless otherwise specified, the issues of these documents are those listedin the issue of the Department of Defense Index of Specifications andStandards(DoDISS) and supplement thereto, cited in the solicitation (see ).SPECIFICATIONS DEPARTMENT OF DEFENSE MIL-C-53072 Chemical Agent Resistant Coating (CARC) System Application Procedures And Quality Control Inspection(Unless otherwise indicated, copies of the above specifications, standards, andhandbooks are available from the Defense Automated Printing Service (DAPS), Building 4D,700 Robbins Avenue, Philadelphia, PA 19111-5094).

6 Non-Government publications. The following documents form a part of thisdocument to the extent specified herein. Unless otherwise specified, the issues ofthe documents which are DoD adopted are those listed in the issue of the DoDISS citedin the solicitation. Unless otherwise specified, the issues of documents not listedin the DoDISS are the issues of the documents cited in the solicitation (see ).AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM) ASTM B117 Operating Salt Spray (Fog) Apparatus (DoD adopted) ASTM F519 Mechanical Hydrogen Embrittlement Testing of Plating Processes and Aircraft Maintenance Chemicals(Application for copies should be addressed to the American Society for Testing andMaterials, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959.)

7 SOCIETY OF AUTOMOTIVE ENGINEERS, INC. (SAE) AMS 2759/9 Hydrogen Embrittlement Relief (Baking) Of Steel Parts(Application for copies should be addressed to the Society Of AutomotiveEngineers, Inc., 400 Commonwealth Drive, Warrendale, PA 15096.) Order of precedence. In the event of a conflict between the text of thisdocument and the references cited herein, the text of this document takesprecedence. Nothing in this document, however, supersedes applicable laws andregulations unless a specific exemption has been 3.

8 REQUIREMENTS Materials. The materials for the blackening processes shall be selected bythe contractor. The selected materials shall result in black coatings meeting allthe applicable requirements of this specification. Preparation of basis metal. Prior to the application of the black coatings,the basis metal shall be thoroughly cleaned. The cleaned surfaces shall be free ofrust, scale, grease, oil, paint, or other foreign matter, and shall pass the waterbreak test described in MIL-C-53072. Cleaning materials and methods shall be at theoption of the contractor.

9 The cleaning process shall be performed withoutmeasurable abrasion or erosion. Stress relief. Unless otherwise specified for a particular end itemspecification or drawing, after forming and hardening, and prior to cleaning andcoating, objectionable residual stress in ferrous alloy parts having a hardnessgreater than 40 HRC shall be relieved by suitable heat treatment. The temperatureshall be such that maximum relief is given without hardness being reduced to lessthan the specified minimum. Stress relief is not necessary where it has beendemonstrated that coating has no harmful effect on the coated part.

10 Coating as a final process. Unless otherwise specified, the black coatingsshall be applied after all machining, forming, welding, cold straightening and heattreatment have been completed. Application of black coatings. The coating shall conform to the classspecified. The specified black coating shall be applied under controlled time andtemperature conditions. All equipment together with solutions or baths shall beproperly maintained and kept free of dirt or possible contaminants. The selectedprocess shall not reduce the hardness of the parts being processed or expose theparts to temperatures in the temper brittle range of the material, nor shall itcause embrittlement of the steel.