Rivolta S.K.D. 4002 - chlc.com.hk

1 Rivolta 4002 High performance at high and low temperature greaseRivolta 4002 is a penetration-stable, water resistant and high temperature-stable synthetic grease, developed for use in heavily loaded roller and plain bearings. Beside aging-resistant synthetic base oils and a special thickener, it also contains a new additive system, that offers an optimal compressive strength at all service Heavily loaded ball-, roller- and needle roller bearings at extreme low and extreme high temperatures.

2 Bearings in evaporate ventilators, frost tunnels, welding machines, drying plants and baker's ovens Bearings in electromotors, ventilators, hot gas ventilators, kilns rolling bearings in calenders or coating machines Guide rolls of transport chains of textile machines Impellers in oven or autoclave carts Plain bearings at high temperature Product Strength Operate in a wide temperature range from -50 C up to+210 C. Optimal at very low and high temperature with constant good lubrication properties Offer aging resistance and penetration stable and thus reduce maintenance and labour costs Resistance to water and can be used in a damp atmosphere and provide excellent protection against corrosion Has good pumpability even at low temperures because of the favourable flow pressuretemperature characteristic.

3 Create an elasto-hydrodynamic lubrication which greatly reduce wear and friction and thus extend the life time of bearings. Appropriate use does not create any risks to the workers health and can also be used in food industry under Germany regulations Biodegradable and environmental friendly. Safe to use Not aggressive to metals, paints, plastics and compatible with seals resistant to mineral 4002 Made in GermanyTechnical dataUnit of 4002 Densityg/mlDIN of base oil at 40 Cmm /sDIN 51562/1100 NLGI-grade-DIN 518182 Worked penetration1/10 mmDIN ISO 2137265-295 PW 100,000 Decrease of worked penetration after 100,000 double cycles1/10 mm-<20 Operative temperature range C--50 to +210 Dropping point CDIN ISO 2176>250 Corrosion protection to steel (SKF-Emcor)

4 518020/0 Corrosion protection to 518111 at 100 Oil separation 40 C%DIN 51817<1 after 18hFlow pressurekPakPaDIN 5180515 at +20 C 55 at -35 Test*Friction coefficient Wear rate ball disc-mm mDIN / / < / < * Swing friction wear tester, temperature loading rises from 50 Cto 100-150-180-210 Cat 2600 N/mm2 with 1,000,000 / 500,000 load changesPacking in 100 g tube, 400 g cartridge, 500 g cartridge, 1 kg tin, 10 kg pail and 25 kg