Technical Data Sheet

1 ^(ValidationDate)613612;6131,2epoxyTechn ical Data SheetPenguard HBProduct descriptionThis is a two component, polyamide cured, high molecular weight epoxy coating. Designed as a high build, all purpose coating for new construction. Can be used as primer, mid coat, finish coat or as single coat system in atmospheric and immersed environments. Suitable for properly prepared carbon steel, stainless steel,aluminium, concrete, galvanised steel, shop primed steel and thermally sprayed zinc , red, white Typical useSuitable for structural steel and piping to be exposed to corrosive environments up to very high and for offshore environments, refineries, power plants, bridges, buildings and mining dataPropertyTest/StandardDescriptionSoli ds by volumeGloss level (GU 60 )ISO 2813 VOC-US/Hong KongUS EPA method 24 (tested)(CARB(SCM)2007, SCAQMD rule 1113, Hong Kong)VOC-EUIED (2010/75/EU) (theoretical)

2 The provided data is typical for factory produced products, subject to slight variation depending on pointISO 3679 Method 125 Cmatt (0-35)395 g/l449 description: According to Jotun Performance Coatings' data is valid for mixed 3233 VOC-ChinaGB/T 23985-2009 (tested)419 g/lVOC-KoreaKorea Clean Air Conservation Act (tested)(Max. thinning ratio included)402 g/l 2 %Film thickness per coatDry film thicknessWet film thicknessTheoretical spreading rateTypical recommended specification m mm /l---Date of issue:22 March 2021 Page: 1/5 This Technical Data Sheet supersedes those previously Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the Application Guide (AG) for this product.

3 For your nearest local Jotun office, please visit our website at Data SheetPenguard HBSurface preparation summary tableSubstrateMinimumRecommendedSt 2 (ISO 8501-1)Carbon steelSa 2 (ISO 8501-1)Stainless steelThe surface shall be hand or machine abraded with non-metallic abrasives or bonded fibre machine or hand abrasive pads to impart a scratch pattern to the blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface surface shall be hand or machine abraded with non-metallic abrasives or bonded fibre machine or hand abrasive pads to impart a scratch pattern to the blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface steelThe surface shall be clean.

4 Dry and appear with a rough and dull blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface primed steelDry, clean and approved inorganic zinc blasted or alternatively blasted to Sa 2 (ISO 8501-1) of at least 70 % of the surfacesClean, dry and undamaged compatible coatingClean, dry and undamaged compatible coatingConcreteMinimum 4 weeks curing. Moisture content maximum 5 %. Mechanically prepare the existing concrete surface by scabbling, needle gun, mechanical disc 4 weeks curing. Moisture content maximum 5 %. Prepare the surface by means of enclosed blast shot or diamond grinding and other appropriate means to abrade the surrounding concrete and to remove preparationApplication methodsThe product can be applied bySpray:Use airless :Recommended for stripe coating and small areas.

5 Care must be taken to achieve the specified dry film preparationTo secure lasting adhesion to the subsequent product all surfaces shall be clean, dry and free from any performance, including adhesion, corrosion protection, heat resistance and chemical resistance is achieved with recommended surface of issue:22 March 2021 Page: 2/5 This Technical Data Sheet supersedes those previously Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the Application Guide (AG) for this product. For your nearest local Jotun office, please visit our website at Data SheetPenguard HBProduct mixing ratio (by volume)Penguard HB Comp A4part(s)part(s)1 Penguard Comp BThinner/Cleaning solventThinner:Jotun Thinner No.

6 17 Nozzle tip (inch/1000):Pressure at nozzle (minimum):Guiding data for airless spray13-23150 bar/2100 psiDrying and Curing timeSurface (touch) dryWalk-on-dry5 h1 h16 h8 h14 d7 d3 dSubstrate temperature10 C23 C40 CDried/cured for serviceDry to over coat, minimum16 h8 hWalk-on-dry: Minimum time before the coating can tolerate normal foot traffic without permanent marks,imprints or other physical and curing times are determined under controlled temperatures and relative humidity below 85 %, and at average of the DFT range for the to over coat, minimum: The recommended shortest time before the next coat can be (touch) dry: The state of drying when slight pressure with a finger does not leave an imprint or reveal for service: Minimum time before the coating can be permanently exposed to the intended maximum overcoating intervals, refer to the Application Guide (AG) for this time and Pot lifePot life8 hInduction time30 minPaint temperature23 CDate of issue:22 March 2021 Page: 3/5 This Technical Data Sheet supersedes those previously Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the Application Guide (AG) for this product.

7 For your nearest local Jotun office, please visit our website at Data SheetPenguard HBNote that the coating will be resistant to various immersion temperatures depending on the specific chemical and whether immersion is constant or intermittent. Heat resistance is influenced by the total coating system. If used as part of a system, ensure all coatings in the system have similar heat , sea waterDry, atmosphericHeat resistance C120 ContinuousPeak140 C50 C50 CPeak temperature duration max. 1 temperatures listed relate to retention of protective properties. Aesthetic properties may suffer at these compatibilityPrevious coat:Subsequent coat:inorganic zinc silicate shop primer, epoxy , epoxy mastic, zinc epoxy , zinc silicateacrylic, epoxy , polyurethane, polysiloxane, vinyl epoxyPackaging (typical)The volume stated is for factory made colours.

8 Note that local variants in pack size and filled volumes can vary due to local of containers(litres)Penguard Comp B1/4 Penguard HB Comp A4/165/201/5 Storage The product must be stored in accordance with national regulations. Keep the containers in a dry, cool, well ventilated space and away from sources of heat and ignition. Containers must be kept tightly closed. Handle with life at 23 C2448 Penguard HB Comp APenguard Comp Bmonth(s)month(s)In some markets commercial shelf life can be dictated shorter by local legislation. The above is minimum shelf life, thereafter the paint quality is subject to (litres)Depending on the actual exposure of the coating system, various primers and topcoats can be used in combination with this product.

9 Some examples are shown below. Contact Jotun for specific system of issue:22 March 2021 Page: 4/5 This Technical Data Sheet supersedes those previously Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the Application Guide (AG) for this product. For your nearest local Jotun office, please visit our website at Data SheetPenguard HBCautionThis product is for professional use only. The applicators and operators shall be trained, experienced and have the capability and equipment to mix/stir and apply the coatings correctly and according to Jotun's Technical documentation. Applicators and operators shall use appropriate personal protection equipment when using this product.

10 This guideline is given based on the current knowledge of the product. Any suggested deviation to suit the site conditions shall be forwarded to the responsible Jotun representative for approval before commencing the and safetyPlease observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not inhale spray mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser, soap and water. Eyes should be well flushed with water and medical attention sought variation When applicable, products primarily meant for use as primers or antifoulings may have slight colour variations from batch to batch.