Technical Data Sheet LOCTITE 406 - paisleyproducts.com

1 TechnicalDataSheet LOCTITE 406 May-2004 PRODUCTDESCRIPTIONLOCTITE 406provides thefollowingproductcharacteristics:Techn ologyCyanoacrylateChemicalTypeEthylcyano acrylateAppearance(uncured)Transparent,c olorlesstostrawcoloredliquidLMSC omponentsOne part- requiresnomixingViscosityLowCureHumidity ApplicationBondingKeySubstratesPlastics andRubbersLOCTITE 406isdesignedforbondingofplasticsandelas tomericmaterialswhereveryfastfixturingis @ 25 ,Cone& Plate,mPa s(cP):Temperature: 25 C,ShearRate:3,000s-112 to22 LMSV iscosity,Brookfield - LVF, 25 C,mPa s(cP):Spindle1, speed30rpm15 to25 FlashPoint- SeeMSDSTYPICALCURINGPERFORMANCEU ndernormalconditions,theatmosphericmoist ureinitiatesthecuringprocess.

2 Althoughfullfunctionalstrengthis developedin a relativelyshorttime,curingcontinuesforat least24hoursbeforefullchemical/solventre sistanceis Thetablebelowshowsthefixturetimeachieved ondifferentmaterialsat 22 C/ 50% definedasthetimetodevelopa shearstrengthof . FixtureTime,ISO4587, seconds:Steel (degreased)10 to20 Aluminum (etched)2 to10 ZincDichromate30 to90 Neoprene<5 Rubber,Nitrile<5 ABS2 to10 PVC2 to10 Polycarbonate15 to50 Phenolic5 Thinbondlinesresultinhighcurespeeds,incr easingthebondgapwilldecreasetherateof Thefollowinggraphshowsthetensilestrength developedwithtimeonBunaN rubberat differentlevelsof Full Cured Strength @ RTCure Time, seconds1007550250010203040506060% RH40% RH20% ,applyingactivatortothesurfacewillimprov ecurespeed.

3 However,thiscanreduceultimatestrengthoft hebondandthereforetestingis recommendedto 24 hours @22 CPhysicalProperties:Coefficientof ThermalExpansion, ASTMD 696, K-180 10-6 Coefficientof ThermalConductivity,ASTMC 177,W/(m K) , ASTME 228, C120 Electrical Properties:DielectricConstant/ DissipationFactor,ASTMD 150 < < < ,ASTMD 257, cm10 1015 SurfaceResistivity,ASTMD 257, 10 1015 DielectricBreakdownStrength,ASTMD 149,kV/mm25 TYPICALPERFORMANCEOFCUREDMATERIALA dhesivePropertiesAfter 24 hours @22 CLapShearStrength,ISO4587:Steel (gritblasted) N/mm 18 to26 (psi) (2,610 to3,770)Aluminum (etched) N/mm 11 to19 (psi) (1,595 to2,755)ZincDichromate N/mm 6 to14 (psi) (870 to2,030)ABS N/mm 4 to6 (psi) (580 to870)PVC N/mm 4 to6 (psi) (580 to870)Polycarbonate N/mm (psi) (510 to650)Phenolic N/mm 5 to15 (psi) (725 to2,175)Neoprene N/mm 5 to15 (psi) (725 to2,175)Nitrile N/mm 5 to15 (psi)

4 (725 to2,175)TDSLOCTITE 406, May-2004 TensileStrength,ISO6922:Steel (gritblasted) N/mm 12 to25 (psi) (1,740 to3,625)Buna-N N/mm 5 to15 (psi) (725 to2,175)After 10 seconds @22 CTensileStrength,ISO6922:Buna-N N/mm (psi) ( 1,000)TYPICALENVIRONMENTAL RESISTANCEC uredfor 1 week @22 CLapShearStrength,ISO4587:MildSteel (gritblasted)HotStrengthTestedat temperature% RT StrengthTemperature, C1007550250050100150 HeatAgingAgedat temperatureindicatedandtested @22 C% Initial Strength at RTHours125100755025001000200030004000500 080 C100 C60 CChemical/SolventResistanceAgedundercond itionsindicatedandtested @22 C.

5 %ofinitialstrengthEnvironment C100hr500hr1000hrMotorOil4010010095 Gasoline22100100100 WaterGlycol50/5022100100100 Ethanol22100100100 Isopropanol22100100100 FreonTA22100100100 Heat/Humidity95%RH40807565 Heat/Humidity95%RHonPolycarbonate4010010 0100 GENERALINFORMATIONT hisproductisnotrecommendedforuseinpureox ygenand/oroxygenrichsystemsandshouldnotb eselectedasa ,consulttheMaterialSafetyDataSheet(MSDS) . thinbondgaps( ). , , 2004. Testreportsforeachbatchareavailableforth eindicatedproperties. LMStestreportsincludeselectedQCtestparam etersconsideredappropriatetospecificatio nsforcustomeruse.

6 Additionally,comprehensivecontrolsareinp lacetoassureproductqualityandconsistency . drylocation. : 2 Cto8 C. Storagebelow2 Corgreaterthan8 Ccanadverselyaffectproductproperties. Materialremovedfromcontainersmaybecontam inatedduringuse. Donotreturnproducttotheoriginalcontainer . additionalinformationis required, ( Cx )+ 32= FkV/mmx V/milmm/ inchesN x lbN/mmx lb/inN/mm x 145= psiMPax 145= psiN m x mm s= cPNoteThedatacontainedhereinarefurnished forinformationonlyandarebelievedtobereli able. Wecannotassumeresponsibilityfortheresult sobtainedbyothersoverwhosemethodswehaven ocontrol.

7 It istheuser'sresponsibilitytodeterminesuit abilityfortheuser' ,HenkelCorporationspecificallydisclaimsa llwarrantiesexpressedorimplied,including warrantiesofmerchantabilityorfitnessfora particularpurpose,arisingfromsaleoruseof HenkelCorporation sproducts. HenkelCorporationspecificallydisclaimsan yliabilityforconsequentialorincidentalda magesofanykind,includinglostprofits. Thediscussionhereinofvariousprocessesorc ompositionsisnottobeHenkelLoctiteAmerica s+ + + 406, May-2004interpretedasrepresentationthatt heyarefreefromdominationofpatentsownedby othersorasa licenseunderanyHenkelCorporationpatentst hatmaycoversuchprocessesorcompositions.

8 Werecommendthateachprospectiveusertesthi sproposedapplicationbeforerepetitiveuse, usingthisdataasa guide. a trademarkof HenkelCorporationReference1 HenkelLoctiteAmericas+ + +