Technical Data Sheet LOCTITE Hysol 1C™ - Ted Pella, Inc.

1 TechnicalDataSheet LOCTITE Hysol 1C September-2007 PRODUCTDESCRIPTIONLOCTITE Hysol 1C provides thefollowingproductcharacteristics:Techn ologyEpoxyChemicalTypeEpoxyAppearance(Re sin)WhiteLMSA ppearance(Hardener)BeigeLMSA ppearance(Mixed)WhiteLMSC omponentsTwopart- Resin& HardenerMixRatio,byweight-Resin: Hardener100: 44 MixRatio,byvolume-Resin: : 1 CureRoomtemperaturecureaftermixingSecond aryCureHeatApplicationBondingSpecificBen efit Machineable Sandable Highservicetemperature Lowoutgassingproperties ExcellentenvironmentalresistanceLOCTITE Hysol 1C isa generalpurposeadhesiveandsealantthatbond s,seals,andrepairsawidevarietyofmaterial sincludingmetals,mostplastics, :SpecificGravity@ 25 SeeMSDSV iscosity@25 C,mPa s(cP)140,000 to330,000 Hardener:SpecificGravity@ 25 SeeMSDSV iscosity@25 C,mPa s(cP)550,000 to870,000 Mixed:SpecificGravity@ 25 @25 C,mPa s(cP)200,000 to500,000 Potlife @25 C, minutes 20 LMSTYPICALPROPERTIESOFCUREDMATERIALC ured @ 25 CexceptwherenotedPhysicalProperties:Coef ficientof ThermalExpansion, ISO11359-2, K-163 10-6 Coefficientof ThermalConductivity, ISO8302,W/(m K) , ISO868, Durometer D:Curedfor2 hours @60 C 65 LMSG lassTransitionTemperature, C98 Electrical Properties:DielectricBreakdownStrength,I EC60243-1, DissipationFactor,IEC60250 :TotalMassLoss,% ,% 3 days @25 CLapShearStrength,ISO4587:Aluminum (etched):Tested@-55 C N/mm (psi) (1,000)Tested@25 C N/mm (psi) (1,750)Tested@82 C N/mm (psi) (1,500)Tested@121 C N/mm (psi) (700)Tested@149 C N/mm (psi) (500)Curedfor 2 hours @60 CLapShearStrength,ISO4587:Aluminum (etched).

2 Tested@-55 C N/mm (psi) (1,500)Tested@25 C N/mm (psi) (2,100)Tested@82 C N/mm (psi) (1,700)Tested@121 C N/mm (psi) (750)Tested@149 C N/mm (psi) (550)GENERALINFORMATIONT hisproductisnotrecommendedforuseinpureox ygenand/oroxygenrichsystemsandshouldnotb eselectedasa sealantforchlorineorotherstrongoxidizing materialsForsafehandlinginformationonthi sproduct,consulttheMaterialSafetyDataShe et(MSDS).TDSLOCTITE Hysol 1C , September-2007 , combinePartA (Resin)andPartB (Hardener) TubeKitshavebeendesignedsothatsqueezingE QUALLENGTHBEADS ofPartA & , ,mixlessthan 900gramsata ,dry, applied,thebondedpartsshouldbeheldincont actuntiltheparthasdevelopedhandlingstren gth(3 to4 hours @25 C)note:thiscanvarywithdifferentbondconfi gurations. It is notnecessarytoclampthepartsunlessmovemen tduringcureis likely. hours @25 Hysol 1C canalsobefullycuredwithheatsuchas;2 hoursat a maximum temperature of60 ,approximately90%offullcurepropertiesare attainedat hour@82 C or20 to30 minutes@121 desireddegreeof curefromhandlingstrengthto fullcure.

3 Is importanttocleanupexcessadhesivefromthew orkareaandapplicationequipmentbeforeit LoctiteMaterialSpecificationLMSLMS datedApril-27, 2005. Testreportsforeachbatchareavailableforth eindicatedproperties. LMStestreportsincludeselectedQCtestparam etersconsideredappropriatetospecificatio nsforcustomeruse. Additionally,comprehensivecontrolsareinp lacetoassureproductqualityandconsistency . Specialcustomerspecificationrequirements maybecoordinatedthroughHenkel drylocation. : 8 Cto21 C. Storagebelow8 Corgreaterthan28 Donotreturnproducttotheoriginalcontainer . additionalinformationis required, ( Cx )+ 32= FkV/mmx V/milmm/ inches m/ milN x lbN/mmx lb/inN/mm x 145= psiMPax 145= psiN m x lb inN mx lb ftN mm oz inmPa s= cPNoteThedatacontainedhereinarefurnished forinformationonlyandarebelievedtobereli able. Wecannotassumeresponsibilityfortheresult sobtainedbyothersoverwhosemethodswehaven ocontrol. It istheuser'sresponsibilitytodeterminesuit abilityfortheuser' ,HenkelCorporationspecificallydisclaimsa llwarrantiesexpressedorimplied,including warrantiesofmerchantabilityorfitnessfora particularpurpose,arisingfromsaleoruseof HenkelCorporation sproducts.

4 HenkelCorporationspecificallydisclaimsan yliabilityforconsequentialorincidentalda magesofanykind,includinglostprofits. Thediscussionhereinofvariousprocessesorc ompositionsisnottobeinterpretedasreprese ntationthattheyarefreefromdominationofpa tentsownedbyothersorasa licenseunderanyHenkelCorporationpatentst hatmaycoversuchprocessesorcompositions. Werecommendthateachprospectiveusertesthi sproposedapplicationbeforerepetitiveuse, usingthisdataasa guide. ,alltrademarksinthisdocumentare trademarksof + + +