Technical Data Sheet LOCTITE STYCAST 2850FT

1 TechnicalDataSheet LOCTITESTYCAST2850FT March-2015 PRODUCTDESCRIPTIONLOCTITESTYCAST2850 FTprovides thefollowingproductcharacteristics:Techn ologyEpoxyAppearance(Resin)BlackProduct Benefits Thermallyconductive Electricallyinsulative Thermalshock resistant LowCTE Canbeusedwitha varietyof catalystsApplicationThermallyconductivee poxyencapsulantTypicalAssemblyApplicatio nsEncapsulatingLOCTITESTYCAST2850 FTisrecommendedforencapsulationofcompone nts LOCTITECAT9,LOCTITECAT11, LOCTITECAT23LV orLOCTITECAT24 LVCATALYST DESCRIPTIONLOCTITECAT9 provides thefollowingproductcharacteristics:Produ ct Benefits Generalpurpose Good chemicalresistance GoodphysicalstrengthCureRoomtemperaturec ureMixRatio,byweight -Material:Catalyst100: ,by Volume -Material:Catalyst100: Temperature-40 to130 CLOCTITECAT11provides thefollowingproductcharacteristics:Produ ct Benefits Longpotlife Excellentchemicalresistance Goodphysicalandchemicalpropertiesat elevatedtemperaturesCureHeatcureMixRatio ,byweight -Material:Catalyst100: ,by Volume -Material:Catalyst100: Temperature-55 to155 CLOCTITECAT23 LVprovides thefollowingproductcharacteristics.

2 Product Benefits Lowcolor Lowviscosity Longpotlife Excellentthermalshockandimpactresistance Excellentlow temperatureproperties Excellentadhesionto glassCureRoomtemperaturecureMixRatio,byw eight -Material:Catalyst100: ,by Volume -Material:Catalyst100: Temperature-65 to105 CLOCTITECAT24 LVprovides thefollowingproductcharacteristics:Produ ct Benefits Low viscosity Excellentadhesion Thermalshockandimpactresistant Excellentlowtemperatureproperties FastcureCureRoomTemperatureMixRatio,bywe ight -Material:Catalyst100: 8 MixRatio,by Volume -Material:Catalyst100: Temperature-65 to105 CTYPICALUNCUREDPROPERTIESLOCTITESTYCAST2 850 FTBrookfieldViscosity, mPa s(cP): Spindle7, Speed10rpm250,000 BrookfieldViscosity - SmallSampleAdapter, mPa s(cP).

3 (EquivalentParameters)Spindle14, speed3 rpm250,000 Density, g/cm @18 to25 C(fromdateofmanufacture), days365 FlashPoint- SeeSDSLOCTITECAT9 Viscosity@25 C,mPa s(cP)92 Density, g/cm SeeSDSLOCTITECAT11 Viscosity@25 C,mPa s(cP)48 FlashPoint- SeeSDSTDSLOCTITESTYCAST2850FT, March-2015 LOCTITECAT23 LVViscosity@25 C,mPa s(cP)25 FlashPoint- SeeSDSLOCTITECAT24 LVViscosity@25 C,mPa s(cP)35 Density, g/cm SeeSDSTYPICALUNCUREDPROPERTIES ASMIXEDLOCTITESTYCAST2850 FTwithLOCTITECAT9 Viscosity@25 C,mPa s(cP)58,000 Density, g/cm , 100 grams, @25 C, minutes45 LOCTITESTYCAST2850 FTwithLOCTITECAT11 Viscosity@25 C,mPa s(cP)64,000 Density, g/cm , 100 grams, @25 C, hours4 LOCTITESTYCAST2850 FTwithLOCTITECAT23 LVViscosity@25 C,mPa s(cP)

4 5,600 Density,, g/cm , 100 grams, @25 C, hour1 LOCTITESTYCAST2850 FTwithLOCTITECAT24 LVWorkLife, 100 grams, @25 C, minutes30 TYPICALCURINGPERFORMANCECureScheduleLOCT ITESTYCAST2850 FTwithLOCTITECAT916 to24 hours@25 C4 to6 hours@45 C1 to2 hours@65 CLOCTITESTYCAST2850 FTwithLOCTITECAT118 to16 hours@80 C2 to4 hours@100 C30 to60 minutes@120 CLOCTITESTYCAST2850 FTwithLOCTITECAT23LV16 to24 hours@25 C4 to6 hours@45 C2 to4 hours@65 CLOCTITESTYCAST2850 FTwithLOCTITECAT24LV8 to16 hours@25 C4 to6 hours@45 C2 hours@65 CForoptimumperformance,followtheinitialc urewitha postcureof2 to4 hoursat (timeandtemperature)mayvarybasedoncustom ers'experienceandtheirapplicationrequire ments,aswellascustomercuringequipment, ,ShoreD96 LinearShrinkage,% (24hrimmersion), % ThermalExpansion:Alpha1, , , C86 ThermalConductivity,W/(m-K) Strength, @25 C, ohm-cm1 1015 OutgassingPropertiesOutgassing, perNASAR eferencePublication1124:Cured24 hours@25 CTML, % , % ,ShoreD96 LinearShrinkage, % (24hrimmersion), % ThermalExpansion:Alpha1, , , C115 ThermalConductivity,W/(m-K) Strength, DissipationFactor:@1 @25 C, ohm-cm1 1015 OutgassingPropertiesOutgassing, perNASAR eferencePublication1124.

5 Samplecured4 hours@80 CTML, % , % ,ShoreD92 LinearShrinkage,, % (24hrimmersion), % ThermalExpansion:Alpha1, , , C68 ThermalConductivity,W/(m-K) @25 C, ohm-cm1 1015 DielectricConstant/ DissipationFactor:@1 Strength, + + + , March-2015 Hardness,ShoreD92 LinearShrinkage,% (24hrimmersion),% ThermalExpansion:Alpha1, ppm47 Alpha2, ppm120 GlassTransitionTemperature(Tg), C39 ThermalConductivity,W/(m-K) @25 C, 1014 SurfaceResistivity, 1015 DielectricConstant/ DissipationFactor:@1 Strength N/mm 92 (psi) (13,300)CompressiveStrength N/mm 155 (psi) (22,500)LOCTITESTYCAST2850 FTwithLOCTITECAT11 MiscellaneousFlexural Strength N/mm 117 (psi) (17,000)CompressiveStrength N/mm 193 (psi) (27,900)LOCTITESTYCAST2850 FTwithLOCTITECAT23 LVMiscellaneousFlexural Strength N/mm 106 (psi) (15,300)CompressiveStrength N/mm 120 (psi) (17,400)GENERALINFORMATIONF orsafehandlinginformationonthisproduct,c onsulttheMaterialSafetyDataSheet,(MSDS).

6 Ifcrystallizationdoesoccur,warmtheconten tsoftheshippingcontainerto50 to60 Cuntilallcrystalshavedissolved. coolto ,dust,moisture,saltandoilswhichcancausep ooradhesionorcorrosionin a ,it is recommendedthatthecontentsoftheshippingc ontainerbethoroughlymixedpriorto preferredto ensurea cleancontainerin therecommendedratio. Weighingapparatushavinganaccuracyinpropo rtionto ,usinga kneadingmotion,for2 to3 minutesandscrapethebottomandsidesofthemi xingcontainerfrequentlyto producea possible,powermixforanadditional2 to3 minutes. Avoidhighmixingspeeds. Thiscan entrapexcessiveamountsofair. It canalso causeoverheatingofthemixture, ,vacuumdeairingordegassingshouldbeperfor medtoremoveany to10 ,add1 to3drops ofanairreleaseagent,suchasANTIFOAM88into 100 gramof , drylocation.

7 Storageinformationmaybeindicatedonthepro ductcontainerlabeling. OptimalStorage: 18 to25 C Materialremovedfromcontainersmaybecontam inatedduringuse. Donotreturnproducttotheoriginalcontainer . required, ( Cx )+ 32= FkV/mmx V/milmm/ inchesN x lbN/mmx lb/inpsi x145= N/mm MPa= N/mm N m x lb inN mx lb ftN mm oz inmPa s= cPAmericas+ + + , March-2015 DisclaimerNote:Theinformationprovidedint hisTechnicalDataSheet(TDS) ,therefore,notliableforthesuitabilityofo urproductfortheproductionprocessesandcon ditionsinrespectofwhichyouusethem, confirmsuchsuitabilityof respectoftheinformationin theTechnicalDataSheetoranyotherwrittenor oralrecommendation(s)regardingtheconcern edproductis excluded,exceptif ,HenkelElectronicMaterialsNV,HenkelNeder landBV,HenkelTechnologiesFranceSASandHen kelFranceSApleaseadditionallynotethefoll owing: IncaseHenkelwouldbeneverthelessheldliabl e,onwhateverlegalground,Henkel sliabilitywillin noeventexceedtheamountof , applicable.

8 TheinformationprovidedinthisTechnicalDat aSheet(TDS) ,therefore,notliableforthesuitabilityofo urproductfortheproductionprocessesandcon ditionsinrespectofwhichyouusethem, confirmsuchsuitabilityof respectoftheinformationin theTechnicalDataSheetoranyotherwrittenor oralrecommendation(s)regardingtheconcern edproductis excluded,exceptif ,ResinTechnologyGroup,Inc.,orHenkelCanad aCorporation, 'sresponsibilitytodeterminesuitabilityfo rtheuser'spurposeofanyproductionmethodsm entionedhereinandtoadoptsuchprecautionsa smaybeadvisablefortheprotectionofpropert yandof personsagainstanyhazardsthatmaybeinvolve din ,HenkelCorporationspecificallydisclaimsa llwarrantiesexpressedorimplied,including warrantiesofmerchantabilityorfitnessfora particularpurpose,arisingfromsaleoruseof HenkelCorporation , ,usingthisdataasa ,alltrademarksinthisdocumentare trademarksof denotesatrademarkregisteredin + + +