Extruded Polystyrene (XPS) Rigid Foam Insulation …

1 FOAMULAR 400/600/1000. Extruded Polystyrene (XPS) Rigid foam Insulation Product Data Sheet R-value year after year even Product Applications following prolonged exposure to Owens Corning FOAMULAR . moisture and freeze/thaw cycling. 400, 600, and 1000 Extruded Polystyrene (XPS) Rigid foam Key Features Insulation are great for under Designed for use in high load slab, cold storage installations, bearing applications. High concrete floors, foundations, compressive strength helps plaza and parking decks, resist damage from heavy loads. roofing, roadways and rail beds, Available in 40, 60 and 100 psi permafrost protection and other compressive strengths. high load-bearing applications Excellent long-term stable Designed for use in high load insulating performance with an bearing applications. High R-value2 of R-5 per inch. compressive strength resists Exceptional moisture resistance, damage from heavy loads.

2 Energy-Saving1, Moisture- Available in 40, 60, and 100 psi Resistant XPS Insulation long-term durability. compressive strengths High Compressive Strength Limited lifetime warranty3 . maintains 90% of R-value Technical Information FOAMULAR 400 XPS. Insulation : ASTM C578 Type VI, and covers all ASTM C578 This product is combustible. A. 40 psi minimum properties. protective barrier or thermal GREENGUARD Gold Certified. barrier is required as specified FOAMULAR 600 XPS in the appropriate building code. Insulation : ASTM C578 Type VII, The only XPS foam with For additional information, consult 60 psi minimum certified recycled content MSDS or contact Owens Corning FOAMULAR 1000 XPS certified by SCS Global Services World Headquarters at Insulation : ASTM C578 Type V, to contain a minimum 20% 1-800-GET-PINK . 100 psi minimum recycled content.

3 Will not corrode, rot or All construction should be Description support mold growth. evaluated for the necessity to Owens Corning FOAMULAR provide vapor retarders. See Zero ozone depletion potential current ASHRAE Handbook of 400, 600 and 1000 are high with 70% less global warming Fundamentals. strength Extruded Polystyrene potential than our previous (XPS) Insulation products formula. FOAMULAR XPS Insulation designed for use in engineered Reusable is a non-structural material and applications requiring additional must be installed on framing load-bearing capability such Lightweight, durable Rigid which is independently braced as under slab, concrete floors, foam panels are easy to handle and structurally adequate to meet foundations, roadways and rail and install. required construction and service beds, plaza and parking decks and Easy to saw, cut or score.

4 Loading conditions. cold storage installations. FOAMULAR XPS Insulation The unique closed-cell structure can be exposed to the exterior of FOAMULAR XPS Insulation during normal construction helps to make it highly resistant cycles. During that time some to moisture, retaining its excellent fading of color may begin due to 1 Savings vary. Find out why in the seller's fact sheet 2 R means the resistance to heat flow; the higher the R-value, the greater the insulating power. UV exposure, and, if exposed for on R-values. Higher R-values mean greater insulating 3 See actual warranty for complete details, limitations extended periods of time, some power. and requirements. FOAMULAR 400/600/1000. Extruded Polystyrene (XPS) Rigid foam Insulation Product Data Sheet degradation or dusting of the Typical Physical Properties1. Polystyrene surface may begin.

5 It FOAMULAR 400/600/1000 Extruded Polystyrene (XPS) Rigid foam Insulation is best if the product is covered FOAMULAR Insulation within 60 days to minimize Test degradation. Once covered, the Property Method2 400 600 1000. Thermal Resistance3, R-Value (180 day) minimum, ASTM C518. deterioration stops, and damage hr ft 2 F/Btu (RSI, C m2 /W). is limited to the thin top surface @ 75 F (24 C) mean temperature 1" Thickness ( ) ( ) . layers of cells. Cells below are 1 " Thickness ( ) ( ). generally unharmed and still 2" Thickness ( ) ( ) ( ). 3" Thickness ( ) ( ) ( ). useful Insulation . @ 40 F ( C) mean temperature 1" Thickness ( ) ( ) . FOAMULAR Extruded 1 " Thickness ( ) ( ). Polystyrene Insulation has a 2" Thickness ( ) ( ) ( ). 3" Thickness ( ) ( ) ( ). maximum service temperature of Long Term Thermal Resistance, LTTR-Value3, minimum 165 F.

6 Taking simple precautions hr ft 2 F/Btu (RSI, C m2 /W). @ 75 F (24 C) mean temperature CAN/ULC. S770-03. during construction can minimize 1" Thickness ( ) ( ) . the potential for heat related 1 " Thickness ( ) ( ). 2" Thickness ( ) ( ) ( ). damage. Install only as much 3" Thickness ( ) ( ) ( ). FOAMULAR XPS Insulation Compressive Strength4, minimum psi (kPa) ASTM D1621 40 (276) 60 (414) 100 (689). as can be covered in the same Flexural Strength5, minimum psi (kPa) ASTM C203 115 (793) 140 (965) 140 (965). day. For horizontal applications, Water Absorption 6, maximum % by volume ASTM C272 always turn the print side down Water Vapor Permeance7, maximum perm (ng/Pa s m2) ASTM E96 (63) (63) (63). so the black print does not show Dimensional Stability, maximum % linear change ASTM D2126 Flame Spread 8, 9 ASTM E84 5 5 5. to the sun which may at times Smoke Developed 8, 9, 10 ASTM E84 45-175 45-175 45-175.

7 Act as a solar collector, raising the Oxygen Index8, minimum % by volume ASTM D2863 24 24 24. temperature of the foam under Service Temperature, maximum F ( C) 165 (74) 165 (74) 165 (74). the print to an unacceptable level. Linear Coefficient of Thermal Expansion, ASTM E228. x 10 -5 ( x 10 -5). Provide a final finish covering in/in/ F (m/m/ C). or temporary white opaque 1. Properties shown are representative values for 1" thick material, unless otherwise specified. 2. Modified as required to meet ASTM C578. covering to avoid possible damage 3. R means the resistance to heat flow; the higher the value, the greater the Insulation power. This Insulation must be installed properly to get the marked R-value. Follow the manufacturer's instructions carefully. If a manufacturer's when dark (non-white) surfaces fact sheet is not provided with the material shipment, request this and review it carefully.

8 R-values vary depending are used over FOAMULAR on many factors including the mean temperature at which the test is conducted, and the age of the sample at the time of testing. Because Rigid foam plastic Insulation products are not all aged in accordance with the same XPS Insulation . Do not cover standards, it is useful to publish comparison R-value data. The R-value for FOAMULAR XPS Insulation is provided FOAMULAR XPS Insulation from testing at two mean temperatures, 40 F and 75 F, and from two aging (conditioning) techniques, 180 day real- time aged (as mandated by ASTM C578) and a method of accelerated aging sometimes called Long Term Thermal either stored (factory wrapped or Resistance (LTTR) per CAN/ULC S770-03. The R-value at 180 day real-time age and 75 F mean temperature is commonly used to compare products and is the value printed on the product.)

9 Unwrapped), or partially installed, 4. Values at yield or 10% deflection, whichever occurs first. with dark colored (non-white), 5. Value at yield or 5%, whichever occurs first. 6. Data ranges from to value shown due to the level of precision of the test method. or clear (non-opaque) coverings 7. Water vapor permeance decreases as thickness increases. 8. These laboratory tests are not intended to describe the hazards presented by this material under actual fire conditions. and leave it exposed to the 9. Data from Underwriters Laboratories Inc. classified. See Classification Certificate U-197. sun. Examples of such coverings 10. ASTM E84 is thickness-dependent, therefore a range of values is given. include but are not limited to filter fabrics, membranes, Owens Corning publication Standards, Codes Compliance temporary tarps, clear number 10015704, "Heat Build Meets ASTM C578 Type polyethylene, etc.

10 If improperly Up Due to Solar Exposure" for VI (FOAMULAR 400. covered, and exposed to the right more information. XPS Insulation ), Type VII. combination of sun, time and (FOAMULAR 600 XPS. temperature, FOAMULAR XPS Insulation ), or Type V. Insulation deformation damage (FOAMULAR 1000 XPS. may occur rapidly. See Insulation ). FOAMULAR 400/600/1000. Extruded Polystyrene (XPS) Rigid foam Insulation Product Data Sheet Product and Packaging Data FOAMULAR 400/600/1000 Extruded Polystyrene (XPS) Rigid foam Insulation Material Packaging Extruded Polystyrene closed-cell foam panel with continuous skin on face and back surface. Shipped in poly-wrapped units with individually wrapped or banded bundles. Product Dimensions Pallet (Unit) Dimensions Square Board Bundles Pieces Pieces Thickness Thickness (in) x Width (in) (typical) Width (ft) x feet per feet per per per per (in) x Length (in) Length (ft) x Height (ft) Pallet Pallet Pallet Bundle Pallet Edges FOAMULAR 400 XPS Insulation 1 1 x 24 x 96 4x8x8 3,072 3,072 8 24 192.