LOCTITE EA 9309NA AERO

1 Technical Process BulletinLOCTITE EA 9309NA AEROE poxy Paste Adhesive(KNOWN AS Hysol EA 9309NA )1 of 5 INTRODUCTIONLOCTITE EA 9309NA AERO is a toughened adhesive ideal for bonding metal, wood, plastics and are flexible and resist water, salt spray and most common fluids. Its outstanding feature is excellent peelstrength to High Peel Strengthx Bonds Many Surfacesx Room Temperature Curex Two ComponentUncured PropertiesPart APart BMixedColorBeigeRedRedViscosity @ 77 F1,500 - 6,000 Poise120 PoiseBrookfield, HBTSpdl 7 @ 20 rpmSpdl 1 @ 100 rpmSpdl 4 @ 20 rpmViscosity @ 25 C150 - 600 Pa Pa s12 Pa sBrookfield, HBTSpdl 7 @ rad/sSpdl 1 @ rad/sSpdl 4 @ rad/sDensity (g/ml) life@ <77 F/25 C1 year1 yearThis material will normally be shipped at ambient conditions, which will not alter our standard warranty,provided that the material is placed into its intended storage upon receipt.

2 Premium shipment is available - This product requires mixing two components together just prior to application to the parts to bebonded. Complete mixing is necessary. The temperature of the separate components prior to mixing is notcritical, but should be close to room temperature (77 F/25 C).Mix RatioPart APart BBy Weight10023 Note: Volume measurement is not recommended for structural applications unless special precautions are takento assure proper Life(450 gram mass) 40 minutes @ 77 F/25 CMethod - ASTM D2471 in water Process BulletinLOCTITE EA 9309NA AEROE poxy Paste Adhesive(KNOWN AS Hysol EA 9309NA )2 of 5 ApplicationMixing - Combine Part A and Part B in the correct ratio and mix thoroughly. THIS IS IMPORTANT! Heatbuildup during or after mixing is normal. Do not mix quantities greater than 1 pound/ 450 grams as dangerousheat buildup can occur causing uncontrolled decomposition of the mixed adhesive.

3 TOXIC FUMES CANOCCUR, RESULTING IN PERSONAL INJURY. Mixing smaller quantities will minimize the heat - Bonding surfaces should be clean, dry and properly prepared. For optimum surface preparationconsult the BONDERITE Surface Preparation Guide. The bonded parts should be held in contact until theadhesive is set. Handling strength for this adhesive will occur in 12 hours @ >77 F/25 C, after which thesupport tooling or pressure used during cure may be removed. Since full bond strength has not yet beenattained, load application should be small at this - This adhesive may be cured for 3 - 5 days @ 77 F/25 C to achieve normal cures up to 200 F/93 C (for small masses only) may be used as an alternative. For example, 1hour @ 180 F/82 C will give complete - It is important to remove excess adhesive from the work area and application equipment before ithardens.

4 Denatured alcohol and many common industrial solvents are suitable for removing uncured with your supplier's information pertaining to the safe and proper use of Strength PerformanceTensile Lap Shear Strength- tested per ASTM D1002. Adherends are aluminum as referenced and treatedwith Phosphoric Acid Anodizing (PAA) per ASTM Results7075-T3 Alclad / PAA3 days @ 77 F/25 C2024-T3 Alclad / PAA1 hour @ 180 F/82 CTest Temperature, F/ Cpsi MPapsi MPa-67/-554, , (Hot/Wet)750 hours @ 160 F/71 C & 85% Roller (Bell) Peel Strength - tested per ASTM D3167. Adherends are aluminum as referenced andtreated with Phosphoric Acid Anodizing (PAA) per ASTM D3933. Bondline line thickness 10 Results2024-T3 Alclad / PAA24 hours @ 77 F/25 Cunder 28 in-Hg2024-T3 Bare / PAA1 hour @ 180 F/82 Cunder 10 psiTest Temperature, F/ Clbf/inN/25mmlbf/inN/25mm77/258939685378 Technical Process BulletinLOCTITE EA 9309NA AEROE poxy Paste Adhesive(KNOWN AS Hysol EA 9309NA )3 of 5T-Peel Strength - tested per ASTM D1876 after curing for 24 hours @ 77 F/25 C under 28 in-Hg.

5 Adherendsare 2024-T3 Alclad aluminum treated with phosphoric acid anodizing per ASTM D3933. Bondline line thickness10 ResultsTest Temperature, F/ Clbf/inN/25mm77/2546205 Service TemperatureService temperature is defined as that temperature at which this adhesive still retains 1000 MPa usingtest method ASTM D1002 and is approximately 160 F/71 Resin PropertiesTensile Properties - tested using mm castings per ASTM D Hardness - Durometer Model D ASTM Properties: Cure 72 hours @ 77 F/25 C & Tested @ 77 F/25 C Tensile Strength4,500 MPa Tensile Modulus338 ksi2,331 MPa Shear Modulus122 ksi841 MPa Poisson's Elongation at Break10% Shore D Hardness80 Thermal PropertyGlass Transition Temperature (Tg) - Rheometric Scientific DMTA IV - Single Cantilever,Heat-up rate: 5 C/min., Frequency: 1 Hz, Strain: Dimensions: 1 mm x mm x mmCure: 72 hours @ 77 F/25 C Tg dry (DMTA)127 F53 C Tg wet (DMTA)147 F64 CCure: 1 hour @ 180 F/82 C Tg dry (DMTA)162 F72 C Tg wet (DMTA)145 F63 C*Wet: 160 F/71 C & 85% RH until saturation.

6 Moisture uptake was Process BulletinLOCTITE EA 9309NA AEROE poxy Paste Adhesive(KNOWN AS Hysol EA 9309NA )4 of 5 Compressive Properties - tested using castings per ASTM Strength @ 77 F/25 C7,000 MPaCompressive Modulus @ 77 F/25 C249 ksi1,716 MPaElectrical Properties - tested per ASTM D149, Constant, 1 KHz, 77 F/25 Factor, 1 KHz, 77 F/25 PrecautionsDo not handle or use until the Material Safety Data Sheet has been read and industrial use INFORMATIOND ispose of spent remover and paint residue per local, state and regional regulations. Refer to HENKELTECHNOLOGIES MATERIAL SAFETY DATA SHEET for additional disposal INFORMATIONG eneral:As with most epoxy based systems, use this product with adequate ventilation. Do not get in eyes or on breathing the vapors. Wash thoroughly with soap and water after handling. Empty containers retainproduct residue and vapors so obey all precautions when handling empty ACAUTION!

7 This material may cause eye and skin irritation or allergic dermatitis. It contains epoxy BWARNING!This material causes eye and skin irritation or allergic dermatitis. It contains using this product refer to container label and HENKEL TECHNOLOGIES MATERIAL SAFETY DATASHEET for additional precautionary, handling and first aid Process BulletinLOCTITE EA 9309NA AEROE poxy Paste Adhesive(KNOWN AS Hysol EA 9309NA )Henkel Corporation Aerospace | 2850 W illow Pass Road | Bay Point, CA 94565 PHONE: + | FAX: + | usageExcept as otherwise noted, all trademarks in this document are trademarks of Henkel Corporation in the and elsewhere. denotes a trademarkregistered in the Patent and Trademark data contained herein are furnished for information only and are believed to be reliable. We cannot assume responsibility for the results obtainedby others over whose methods we have no control.

8 It is the user's responsibility to determine suitability for the user's purpose of any productionmethods mentioned herein and to adopt such precautions as may be advisable for the protection of property and of persons against any hazards thatmay be involved in the handling and use thereof. In light of the foregoing,Henkel Corporationspecifically disclaims all warranties expressed orimplied,including warranties of merchantability or fitness for aparticular purpose, arising from sale or use of Henkel Corporation sproducts. Henkel Corporation specifically disclaims any liability for consequential or incidental damages of any kind, including lost discussionherein of various processes or compositions is not to beinterpreted as representation that they are free fromdomination of patentsowned by others or as a license underany Henkel Corporation patents that may cover suchprocesses or compositions.

9 We recommend that eachprospective user test his proposed application before repetitive use, using this data as a guide. This product may be covered by one or more UnitedStates or foreign patents or patent of 5 NoteThe data contained herein are furnished for information only and are believed to be reliable. We cannotassume responsibility for the results obtained by others over whose methods we have no control. It is theuser's responsibility to determine suitability for the user's purpose of any production methods mentioned hereinand to adopt such precautions as may be advisable for the protection of property and of persons against anyhazards that may be involved in the handling and use thereof. In light of the foregoing,Henkel Corporationspecifically disclaims all warranties expressed or implied, including warranties ofmerchantability orfitness for a particular purpose, arising from sale or use of Henkel Corporation s products.

10 HenkelCorporation specifically disclaims any liability for consequential or incidental damages of any kind,includinglost discussion herein of various processes or compositions is not to be interpreted asrepresentation that they are free from domination of patents owned by others or as a license under any HenkelCorporation patents that may cover such processes or compositions. We recommend that each prospectiveuser test his proposed application before repetitive use, using this data as a guide. This product may becovered by one or more United States or foreign patents or patent 7/2013