Thermoplastic Polyurethane Elastomers (TPU) - BASF

1 Thermoplastic Polyurethane Elastomers (TPU)Elastollan Product RangeElastollan Elastollan is the brand name for Thermoplastic Polyurethane (TPU) from basf . It stands for maximum reliability, consistent product quality and cost efficiency. Elastollan can be extruded into hoses, cable sheathing, belts, films and profiles, and can also be processed using blow molding and injection molding technologies. Over the last few decades, the numerous benefits of Elastollan in all its forms aromatic or aliphatic, very soft or glass fiber-reinforced, flame retardant or highly transparent have been clearly demonstrated across every sector of extensive product portfolio, which makes use of a variety of raw materials and formulations, is the starting point for successfully bringing innovative customer projects to thrive on creative ideas and complex challenges come andtalk to us!

2 Elastollan Nomenclature and Portfolio11 Series12 SeriesFHF / HFFR SeriesC SeriesB SeriesS Series500 Series800 SeriesA SeriesL SeriesSoft ProductsHPM Series (aliphatic)HPM Series (aromatic)R SeriesFood Contact SeriesSpecial ProductsSpecial Products Infinergy Bondura SeriesHotbond Series0406081012141618 19202122 24262830 32 34 36 384 SeriesThe letter or num-ber characterizes the polyol baseB, C, S, Soft, 5, 6, 7, 8, 9 = polyester base10, 11, 12, 13 = polyether baseR = glass fiber-reinforcedSP = special productN = based onrenewable resourcesEXP = experimen- tal gradeElastollan The registered trade mark of basf for Thermoplastic polyurethaneElastollan A and L stand for aliphatic Thermoplastic polyurethanesInfinergy HotbondBonduraShore HardnessShore hardness A (35 - 98)Shore hardness D (47 - 83)

3 Granule Shape1 = cylindrical orlentil-shaped5 = diced granulesLubricant0, 1 = no added lubricants2, 3, 5, 9 = addedlubricantsAdditivesESD = electronicsensitive devicesFC = food contactFHF/HFFR = flame retardant. halogen-freeHPM = high per-formance materialM = mat surfaceN = non- stabilizedQ = compoundsP/W = contains plasticizersT = approved fordrinking water applicationsU = UV-stabilizedAdditives000 = natural TSG = TPU forexpansionElastollan NomenclatureNomenclature Elastollan 11 85 A 10 W 0005 Elastollan PortfolioPortfolio Product RangeChemistryshore HardnessRange Properties11 Ether70 A - 75 DExcellent hydrolysis resistance, cold flexibility, resistance to microorganisms11 FHFE ther flameretardant75 A - 54 DNon-halogen-based flame retardant, outstanding mechanical properties, excellent hydrolysis resistance, resistance to microorganisms12 Ether85 A - 83 DHighly transparent, excellent hydrolysis resistance.

4 Cold flexibility, resistance to microorganisms12 FHFE ther flameretardant70 D - 80 DNon-halogen-based flame retardant, outstanding mechanical properties, high rigidity, excellent hydrolysis resistance, resistance to microorganisms13 Ether85 A - 90 AWater-vapor permeable, good tear propagation strength, very good mechanical properties CEster80 A - 75 DExcellent mechanical properties, very good damping behavior, good rebound, very good wear resistanceBEster80 A - 65 DVery good mechanical properties, good cold flexibility, good wear resistance SEster70 A - 65 DGood mechanical properties, good wear resistance, good damping behavior and rebound500 Ester85 A - 65 DGood mechanical properties, good abrasion resistance600 Ester70 A - 50 DTransparent, good damping behavior and rebound700 Ester70 A - 65 DVery good hydrolysis resistance, high wear resistance, very low compression set, very good mechanical properties800 Ester75 A - 95 AVery good transparency, good abrasion resistanceAEther or esteraliphatic 65 A - 55 DColor-fast, non-yellowing, hydrolysis-resistant (ether)

5 LEther or esteraliphatic 75 A - 80 DTransparent, long-term UV-stabilitySupersoftEster or ether35 A - 65 AVery good wet grip, very flexible, very soft in part, highly transparent in part, ESD grades with very good volume resistivityHPME ster60 A - 55 DVery good damping behavior and rebound, high temperature resistance, improved setting behavior, good demolding properties, color-fast, soft touchHFFRE ther flame retardant85 A - 92 ANon-halogen-based flame retardant, increased flame retardancy, reduced smoke density and toxicityCSEster70 A - 65 DVery good compression set, extremely low creep behavior REster-reinforcedE-modulus 1000 - 17000 MPaGlass fiber-reinforced, very high stiffness, low thermal expansion coefficient, low shrinkage, very good impact resistanceFood Contact (FC) Ester or ether70 A - 75 DBasic suitability for food contact applications in FDA and EU-regulated markets (see Food Contact Information)HotbondEsterSee tech.

6 Product informationExcellent adhesive properties, good solubility with a broad viscosity rangeBonduraEsterSee tech. product informationExcellent adhesive properties, low activation temperature, good solubility with a broad viscosity range6 Elastollan 11 SeriesElastollan 11 Series Thermoplastic polyether Polyurethane elastomerPropertyUnit of Measurementtest Procedure1170 a 101175 a 10 W1180 a 101185 a 10 W1185 a 101185 a 59 U1185 a 10 M1185 a 12 WMHardnessShore ADIN ISO 7619-1 (3s) 7175808387868887 HardnessShore DDIN ISO 7619-1 (3s)363939 Densityg/cm DIN EN ISO strengthMPaDIN 53504-S23040454045504530 Elongation at break%DIN 53504-S2850700650700600480600650 Stress at 20 % elongationMPaDIN at 100 % elongationMPaDIN at 300 % elongationMPaDIN from tensile testMPaDIN EN ISO 527 Tear strengthkN/mDIN ISO (b)

7 4540555070656055 Abrasionmm DIN ISO 4649-A4545304525356065 Compression set 23 C / 72 hours%DIN ISO 81520202520253525 Compression set 70 C / 24 hours%DIN ISO 81539404535454543 Tensile strength after storage in water at 80 C for 42 daysMPaDIN 53504-S220283030323030 Elongation at break after storage in water at 80 C for 42 days%DIN 53504-S2900750700700600650600 Notched impact resistance (Charpy) +23 CNotched impact resistance (Charpy) -30 CkJ/m kJ/m DIN EN ISO 179-1nb nbnb nbnb nbnb nbnb nbnb nbnb nbBurning behavior (depending on wall thickness)UL 94V0 / V2 HBV2 HBV2 PropertyUnit of Measurementtest Procedure1190 a 101195 a 101195 a 55 U1198 a 101154 D 101160 D 501164 D 111174 D 11 HardnessShore ADIN ISO 7619-1 (3s)9296 HardnessShore DDIN ISO 7619-1 (3s)4248435253606975 Densityg/cm DIN EN ISO strengthMPaDIN 53504-S25055505050505065 Elongation at break%DIN 53504-S2550500500420450400350380 Stress at 20 % elongationMPaDIN 53504-S2566911131625 Stress at 100 % elongationMPaDIN 53504-S2910101517192530 Stress at 300 % elongationMPaDIN 53504-S216181828384145450E-modulus from tensile testMPaDIN EN ISO 527150200250560 Tear strengthkN/mDIN ISO (b)

8 85100100130150170190220 Abrasionmm DIN ISO 4649-A2525252530303022 Compression set 23 C / 72 hours%DIN ISO 8152530303540404050 Compression set 70 C / 24 hours%DIN ISO 8154545455050505055 Tensile strength after storage in water at 80 C for 42 daysMPaDIN 53504-S23537373535353535 Elongation at break after storage in water at 80 C for 42 days%DIN 53504-S2600500500450450450400400 Notched impact resistance (Charpy) +23 CNotched impact resistance (Charpy) -30 CkJ/m kJ/m DIN EN ISO 179-1nb nbnb nbnb nbnb 190nb 18nb 16nb 12nb 5 Burning behavior (depending on wall thickness)UL 94 HBFor more detailed information, please refer to the product information and processing 11 SeriesPropertyUnit of Measurementtest Procedure1170 a 101175 a 10 W1180 a 101185 a 10 W1185 a 101185 a 59 U1185 a 10 M1185 a 12 WMHardnessShore ADIN ISO 7619-1 (3s) 7175808387868887 HardnessShore DDIN ISO 7619-1 (3s)363939 Densityg/cm DIN EN ISO strengthMPaDIN 53504-S23040454045504530 Elongation at break%DIN 53504-S2850700650700600480600650 Stress at 20 % elongationMPaDIN at 100 % elongationMPaDIN at 300 % elongationMPaDIN from tensile testMPaDIN EN ISO 527 Tear strengthkN/mDIN ISO (b)

9 4540555070656055 Abrasionmm DIN ISO 4649-A4545304525356065 Compression set 23 C / 72 hours%DIN ISO 81520202520253525 Compression set 70 C / 24 hours%DIN ISO 81539404535454543 Tensile strength after storage in water at 80 C for 42 daysMPaDIN 53504-S220283030323030 Elongation at break after storage in water at 80 C for 42 days%DIN 53504-S2900750700700600650600 Notched impact resistance (Charpy) +23 CNotched impact resistance (Charpy) -30 CkJ/m kJ/m DIN EN ISO 179-1nb nbnb nbnb nbnb nbnb nbnb nbnb nbBurning behavior (depending on wall thickness)UL 94V0 / V2 HBV2 HBV2 PropertyUnit of Measurementtest Procedure1190 a 101195 a 101195 a 55 U1198 a 101154 D 101160 D 501164 D 111174 D 11 HardnessShore ADIN ISO 7619-1 (3s)9296 HardnessShore DDIN ISO 7619-1 (3s)4248435253606975 Densityg/cm DIN EN ISO strengthMPaDIN 53504-S25055505050505065 Elongation at break%DIN 53504-S2550500500420450400350380 Stress at 20 % elongationMPaDIN 53504-S2566911131625 Stress at 100 % elongationMPaDIN 53504-S2910101517192530 Stress at 300 % elongationMPaDIN 53504-S216181828384145450E-modulus from tensile testMPaDIN EN ISO 527150200250560 Tear strengthkN/mDIN ISO (b)

10 85100100130150170190220 Abrasionmm DIN ISO 4649-A2525252530303022 Compression set 23 C / 72 hours%DIN ISO 8152530303540404050 Compression set 70 C / 24 hours%DIN ISO 8154545455050505055 Tensile strength after storage in water at 80 C for 42 daysMPaDIN 53504-S23537373535353535 Elongation at break after storage in water at 80 C for 42 days%DIN 53504-S2600500500450450450400400 Notched impact resistance (Charpy) +23 CNotched impact resistance (Charpy) -30 CkJ/m kJ/m DIN EN ISO 179-1nb nbnb nbnb nbnb 190nb 18nb 16nb 12nb 5 Burning behavior (depending on wall thickness)UL 94HB Excellent hydrolysis resistance Cold flexibility Resistance to microorganisms8 Elastollan 12 SeriesElastollan 12 SeriesThermoplastic polyether Polyurethane elastomerPropertyUnit of Measurementtest Procedure1285 a 10 U1290 a 10 U1295 a 13 U1298 a 13 U1254 D 13 U1260 D 13 U1264 D 13 U1278 D 11 U1283 D 11 UHardnessShore ADIN ISO 7619-1 (3s)868995 HardnessShore DDIN ISO 7619-1 (3s)